Laminate comprising a polyolefin layer adhered to a base layer
Laminate containing a polyolefin layer adhered to a base layer. The polyolefin layer contains a blend of 90-99.7 wt % of a copolymer comprising 80-98 wt % of propylene and 2-20 wt % of C 2 -C 10 α-olefin units, and 0.3-10 wt % of a polyethylene having a density of 870-920 kg/m 3 or less. The base layer includes a propylene homopolymer or a copolymer of propylene and up to 5 wt % of C 2 -C 10 alpha-olefin units other than propylene.
1. Laminate comprising a polyolefin layer adhered to a base layer, the polyolefin layer comprising a blend of 90-99.7 wt % of a copolymer comprising 80-98 wt % of propylene and 2-20 wt % of C 2 -C 10 α-olefin units, and 0.3-10 wt % of a polyethylene having a density of 870-920 kg/m 3 or less, and the base layer comprising a propylene homopolymer or a copolymer of propylene and up to 5 wt % of C 2 -C 10 alpha-olefin units other than propylene.
2. Laminate according to claim 1 , wherein deposited on the opposite surface of the polyolefin layer from the base layer is a metal layer.
3. Laminate according to claim 1 , wherein the polyethylene has a melt index MI 2 measured according to ISO Standard 1133 (190° C., 2.16 kg) of 2-30 g/10 min.
4. Laminate according to claim 1 , wherein the polyethylene has a melt index MI 2 measured according to ISO Standard 1133 (190° C., 2.16 kg) of 3-20 g/10 min.
5. Laminate according to claim 1 , wherein the polyethylene has a molecular weight distribution (Mw/Mn) of 2-4.
6. Laminate according to claim 1 , wherein the polyethylene is made using a metallocene catalyst.
7. Laminate according claim 1 , wherein the propylene-α-olefin copolymer of the polyolefin layer is a copolymer of propylene and ethylene and/or 1-butene.
8. Laminate according claim 1 , wherein the propylene-α-olefin copolymer of the polyolefin layer is a copolymer of propylene and 3-5 wt % of ethylene or a copolymer of propylene and 5-8 wt % of 1-butene.
9. Laminate according claim 1 , wherein the propylene-α-olefin copolymer of the polyolefin layer contains 4-15 wt % of 1-butene and also 0.3-3 wt % ethylene.
10. Laminate according to claim 1 , which is oriented by stretching in at least one of machine direction and transverse direction.
11. Laminate according to claim 10 , wherein the stretching ratios are 2 to 10 in the machine direction and 5 to 15 in the transverse direction.
12. Laminate according to claim 1 , wherein the thickness of the polyolefin layer when adhered to a further layer is 0.6-3 μm.
13. Laminate according to claim 1 , which comprises at least one further layer adhered to the surface of the base layer opposite that to which the polyolefin layer is adhered.
14. Laminate according claim 9 , wherein the propylene-α-olefin copolymer of the polyolefin layer contains 10-14 wt % 1-butene and 0.5-2 wt % ethylene.