Thermoset polyurethanes based on moisture-resistant polyols for use in golf balls
View Patent ↗The present invention provides golf balls having a rubber core, and a cover layer made from a thermoset polyurethane of polyurethane-urea that is the reaction product of a polyisocyanate with moisture-resistant polyol and curing agent. An intermediate layer, formed from an olefin-based acid copolymer ionomer composition and preferably an ethylene acid copolymer, is disposed between the rubber core and cover. The moisture-resistant polyol is preferably a reaction product of dimer acid or dimer ester and a polyolefin diol, or a polybutadiene polyol, or a polyisoprene. Preferably, the cover layer has a moisture vapor transmission rate (MVTR) between 3 grams·mm/m 2 ·day to 4 grams·mm/m 2 ·day.
1. A golf ball, comprising:
a core having a first Shore C surface hardness of C 1 in the range of 50 to 90, the core being formed from a rubber composition;
an intermediate layer surrounding the core, the intermediate layer being formed from a olefin-based acid copolymer ionomer composition and having a hardness in the range of 30 to 90 Shore D; and
a cover layer surrounding the intermediate layer having a second Shore C surface hardness of C 2 in the range of 60 to 95, the cover layer being formed from a thermoset polyurethane or polyurethane-urea composition that is produced by a reaction of: i) an isocyanate compound, ii) a moisture-resistant polyol having a weight average molecular weight in the range of 500 to 10,000 grams per mole, and iii) a curing agent selected from hydroxyl-terminated or amine-terminated curing agents, and mixtures thereof, and wherein the ratio of C 2 to C 1 is in the range of 0.6 to 1.4, wherein the cover layer has a moisture vapor transmission rate between 3 grams·mm/m 2 ·day to 4 grams·mm/m 2 ·day.
2. The golf ball of claim 1 , wherein the rubber composition is selected from the group consisting of polybutadiene, polyisoprene, natural rubber, ethylene-propylene, ethylene-propylene diene, and styrene-butadiene rubbers, and mixtures thereof.
3. The golf ball of claim 2 , wherein the rubber composition is polybutadiene rubber.
4. The golf ball of claim 1 , wherein the olefin-based acid copolymer ionomer composition is an ethylene based acid copolymer.
5. The golf ball of claim 1 , wherein the olefin-based add copolymer contains acid groups selected from the group consisting of methacrylic, acrylic, maleic, crotonic, fumaric, and itaconic add.
6. The golf ball of claim 5 , wherein the olefin-based acid copolymer contains acid groups in an amount of 16 wt. % or less.
7. The golf ball of claim 5 , wherein the olefin-based add copolymer contains acid groups in an amount of greater than 16 wt. %.
8. The golf ball of claim 1 , wherein the add groups of the olefin-based add copolymer are neutralized to a neutralization level of 10 to 80%.
9. The golf ball of claim 5 , wherein the add groups of the olefin-based acid copolymer are neutralized to a neutralization level of 80 to 100%.
10. A golf ball, comprising:
a core having an inner core and outer core layer, the inner core having a first Shore C surface hardness of C 1 in the range of 50 to 90, and the outer core layer having a Shore D surface hardness in the range of about 50 to about 90;
an intermediate layer surrounding the core, the intermediate layer being formed from a olefin-based add copolymer ionomer composition and having a hardness in the range of 30 to 90 Shore D; and
a cover layer surrounding the intermediate layer having a second Shore C surface hardness of C 2 in the range of 60 to 95, the cover layer being formed from a thermoset polyurethane or polyurethane-urea composition that is produced by a reaction of: i) an isocyanate compound, ii) a moisture-resistant polyol having a weight average molecular weight in the range of 500 to 10,000 grams per mole, and iii) a curing agent selected from hydroxyl-terminated or amine-terminated curing agents, and mixtures thereof, and wherein the ratio of C 2 to C 1 is in the range of 0.6 to 1.4, wherein the cover layer has a moisture vapor transmission rate between 3 grams·mm/m 2 ·day to 4 grams·mm/m 2 ·day.