Two-coat single cure powder coating
Methods and systems for coating metal substrates are provided. The methods and systems include sequential application of low flow and high flow powder coatings followed by a single heating step to provide a cured coating. The methods and systems include a marker that allows coating uniformity to be monitored and assessed during application. The described methods provide coatings with optimal surface smoothness and edge coverage.
1. A method, comprising:
providing a metal substrate;
applying a primer coating by a corona charging process of electrostatic spray, the primer coating comprising a first powder coating composition comprising a marker and a carboxyl-functional polyester binder resin;
applying a topcoat by a corona charging process of electrostatic spray directly to the primer coating, such that the primer coating has not been pre-heated or cured, the topcoat comprising a second powder coating; and
curing the primer coating and the topcoat to form a continuous corrosion-resistant coating by heating the metal substrate with the primer coating and topcoat applied thereon in a single step, without multiple heating cycles,
wherein the uniformity of the topcoat is assessed by monitoring the marker in the primer coating; and the coated metal substrate has a surface smoothness of 25% to 90% when measured as 20-degree gloss.
2. The method of claim 1 , wherein the first coating composition has a flow of about 15 mm to 40 mm.
3. The method of claim 1 , wherein the first coating composition has a flow of about 20 to 35 mm.
4. The method of claim 1 , wherein the second coating composition has flow of greater than about 50 mm.
5. The method of claim 1 , wherein the second coating composition has flow of greater than about 70 mm.
6. The method of claim 1 , wherein the second coating composition has flow of greater than about 75 mm.
7. The method of claim 1 , wherein the marker is a uv-sensitive pigment or uv-sensitive dye.
8. The method of claim 1 , wherein the marker is a pigment that undergoes a color change on heating.
9. The method of claim 1 , wherein the marker is a detectable component visible under a black light.
10. The method of claim 1 , wherein the first coating composition and second coating composition have a color difference of less than about 5 units on at least one color axis L, a, orb.
11. The method of claim 1 , wherein the color difference between the continuous film before the single heating step and after the single heating step is at least about 15 units on at least one color axis L, a, or b.
12. The method of claim 1 , wherein the metal substrate with the primer and topcoat applied thereon is heated in a single step at a temperature of about 180° C. to 200° C.
13. The method of claim 1 , wherein the metal substrate with the primer coating and topcoat applied thereon is heated in a single step at a temperature of about 140° C. to 170° C.
14. The method of claim 1 , wherein the metal substrate with the primer coating and topcoat applied thereon is heated in a single step at a temperature of about 120° C. to 135° C.
15. The method of claim 1 , wherein the primer coating is applied at a film build of about 20 to 40 micron.
16. The method of claim 1 , wherein the topcoat is applied at a film build of about 25 to 35 micron.
17. A method, comprising of:
providing a metal substrate;
applying a first powder coating composition by a corona charging process of electrostatic spray, the first powder coating composition comprising of a marker and a polymer binder resin and having a viscosity of no more than 500 to 3000 Pa;
applying a second powder coating by a corona charging process of electrostatic spray, the second powder coating comprising of a polymer binder resin and having a viscosity of at least 3000 Pa; and
curing the metal substrate after the application of both the first powder coating and the second powder coating by heating the metal substrate in a single step, to form a continuous corrosion-resistant coating with edge coverage of about 10% of face coverage.
18. A method, consisting of:
providing a metal substrate;
applying a first powder coating composition to the metal substrate by a tribo charging process of electrostatic spray, the first powder coating composition comprising of a marker and a polymer binder resin;
applying a second powder coating to the first powder coating by a tribo charging process of electrostatic spray, such that the first powder coating is not pre-heated or cured before applying the second powder coating, the uniformity of the second powder coating being assessed by monitoring the marker in the first powder coating; and
curing the metal substrate after the application of both the first powder coating and the second powder by heating the metal substrate in a single step, to form a continuous corrosion-resistant coating with edge coverage of about 10% of face coverage.
19. A method, comprising:
providing a metal substrate;
applying a primer coating by a tribo charging process of electrostatic spray, the primer coating comprising a first powder coating composition comprising a marker and a carboxyl-functional polyester binder resin;
applying a topcoat by a tribo charging process of electrostatic spray directly to the primer coating, such that the primer coating has not been pre-heated or cured, the topcoat comprising a second powder coating; and
curing the primer coating and the topcoat to form a continuous corrosion-resistant coating by heating the metal substrate with the primer coating and topcoat applied thereon in a single step, without multiple heating cycles,
wherein the uniformity of the topcoat is assessed by monitoring the marker in the primer coating; and the coated metal substrate has a surface smoothness of 25% to 90% when measured as 20-degree gloss.