View Patent ↗A method for vitrification of waste to reduce the formation of persistent secondary phases comprising separating at least one glass frit constituent from an initial glass frit to form a modified glass frit. The waste, modified glass frit, and the at least one glass frit constituent are mixed together with the modified glass frit and the at least one glass frit constituent being added as separate components. The resulting mixture is vitrified.
1. A method for vitrification of waste comprising:
mixing the waste, a glass frit additive, and at least one glass frit constituent including Al 2 O 3 , B 2 O 3 , and/or SiO 2 to form a mixture, the glass frit additive and the at least one glass frit constituent being added as separate components to the mixture; and
vitrifying the mixture in a melter.
2. The method of claim 1 wherein the glass frit additive is in the form of glass beads, cylindrical glass fiber cartridges, glass powder, and/or glass flakes.
3. The method of claim 1 comprising separating at least a portion of Al 2 O 3 , B 2 O 3 , and/or SiO 2 from an initial glass frit, wherein the at least one glass frit constituent includes the separated Al 2 O 3 , B 2 O 3 , and/or SiO 2 .
4. The method of claim 1 comprising separating at least a portion of Al 2 O 3 , B 2 O 3 , and/or SiO 2 from an initial glass frit to form a modified glass frit, wherein the glass frit additive includes the modified glass frit and the at least one glass frit constituent includes the separated Al 2 O 3 , B 2 O 3 , and/or SiO 2 .
5. The method of claim 4 wherein the separated Al 2 O 3 , B 2 O 3 , and/or SiO 2 includes at least approximately all of the Al 2 O 3 and at least a portion of the B 2 O 3 in the initial glass frit.
6. The method of claim 5 wherein the separated Al 2 O 3 , B 2 O 3 , and/or SiO 2 includes at least a portion of the SiO 2 in the initial glass frit.
7. The method of claim 4 wherein the separated Al 2 O 3 , B 2 O 3 , and/or SiO 2 includes Al 2 O 3 and B 2 O 3 from the initial glass frit in an amount totaling at least approximately 7 wt % of the initial glass frit.
8. The method of claim 1 comprising mixing the waste, the glass frit additive, and the at least one glass frit constituent together in the melter.
9. The method of claim 1 comprising mixing the waste, the glass frit additive, and the at least one glass frit constituent together before entering the melter.
10. The method of claim 1 comprising mixing the waste and the at least one glass frit constituent together before entering the melter.
11. The method of claim 1 wherein the waste, the glass frit additive, and the at least one glass frit constituent are in powder form.
12. The method of claim 1 wherein the waste includes nuclear waste.
13. The method of claim 1 wherein the waste includes radioactive waste.
14. The method of claim 1 wherein the waste includes high level radioactive waste.
15. The method of claim 1 wherein the melter includes a joule heated ceramic melter.
16. The method of claim 1 wherein the melter includes a cold crucible melter and/or an induction melter.
17. The method of claim 1 wherein the mixture comprises:
approximately 70 wt % to 78 wt % of the glass frit additive; and
approximately 7 wt % to 15 wt % of the at least one glass frit constituent.
18. A method for vitrification of waste comprising:
separating at least one glass frit constituent from an initial glass frit to form a modified glass frit;
mixing the waste, the modified glass frit, and the at least one glass frit constituent to form a mixture, the modified glass frit and the at least one glass frit constituent being added as separate components to the mixture; and
vitrifying the mixture in a melter.
19. The method of claim 18 wherein the at least one glass frit constituent includes approximately 7 wt % to 15 wt % of the initial glass frit.
20. The method of claim 18 wherein the at least one glass frit constituent includes Al 2 O 3 , B 2 O 3 , and/or SiO 2 .
21. The method of claim 18 wherein the at least one glass frit constituent includes at least approximately all of the Al 2 O 3 and at least a portion of the B 2 O 3 in the initial glass frit.
22. The method of claim 21 wherein the at least one glass frit constituent includes at least a portion of the SiO 2 in the initial glass frit.
23. The method of claim 18 wherein the at least one glass frit constituent includes Al 2 O 3 and B 2 O 3 from the initial glass frit in an amount totaling at least approximately 7 wt % of the initial glass frit.
24. The method of claim 18 wherein the waste, the modified glass frit, and the at least one glass frit constituent are in powder form.
25. The method of claim 18 wherein the waste includes nuclear waste.
26. The method of claim 18 wherein the waste includes radioactive waste.
27. The method of claim 18 wherein the waste includes high level radioactive waste.
28. The method of claim 18 wherein the melter includes a joule heated ceramic melter.
29. The method of claim 18 wherein the melter includes a cold crucible melter and/or an induction melter.
30. The method of claim 18 wherein the mixture comprises:
approximately 70 wt % to 78 wt % of the modified glass frit; and
approximately 7 wt % to 15 wt % of the at least one glass frit constituent.