REDUCTION GEAR FOR ELECTRIC POWER STEERING AND METHOD FOR MANUFACTURING THE SAME
A reduction gear for electric power steering includes a first reduction gear composition for electric power steering containing 95 to 97 parts by weight of polyamide 66 (PA66) among polyamide-based materials, and a second reduction gear composition for electric power steering containing 3 to 5 parts by weight of an ethylene-methacrylic acid copolymer (EMAA) among polyolefin-based materials, wherein a weight ratio of the PA66 to the EMAA is 24:1 to 49:1. A method for manufacturing a reduction gear for electric power steering includes adding a first reduction gear composition for electric power steering comprising 95 to 97 parts by weight of PA66 among polyamide-based materials and a second reduction gear composition for electric power steering containing 3 to 5 parts by weight of an EMAA among polyolefin-based materials to a heater having a melting temperature of 250° C. to 260° C. for 2 to 3 minutes, to prepare a mix composition containing the PA66 and the EMAA in a weight ratio of 24:1 to 49:1, injecting a material including the mix composition using an injector at 270° C. to 280° C., and cooling the injected material including the mix composition at room temperature.
1 . A reduction gear for electric power steering comprising:
a first reduction gear composition for electric power steering comprising 95 to 97 parts by weight of polyamide 66 (PA66) among polyamide-based materials; and
a second reduction gear composition for electric power steering comprising 3 to 5 parts by weight of an ethylene-methacrylic acid copolymer (EMAA) among polyolefin-based materials,
wherein a weight ratio of the polyamide 66 (PA66) to the ethylene-methacrylic acid copolymer (EMAA) is 24:1 to 49:1.
2 . A reduction gear for electric power steering comprising:
a first reduction gear composition for electric power steering comprising 95 to 97 parts by weight of polyamide 66 (PA66) among polyamide-based materials; and
a third reduction gear composition for electric power steering comprising 3 to 5 parts by weight of linear low-density polyethylene (LLDPE) among polyolefin-based materials,
wherein a weight ratio of the polyamide 66 (PA66) and the linear low-density polyethylene (LLDPE) is 24:1 to 49:1.
3 . A reduction gear for electric power steering comprising:
a first reduction gear composition for electric power steering comprising 95 to 97 parts by weight of polyamide 66 (PA66) among polyamide-based materials; and
a fourth reduction gear composition for electric power steering comprising 3 to 5 parts by weight of ethylene vinyl acetate (EVA) among polyolefin-based materials, wherein a weight ratio of the polyamide 66 (PA66) and the ethylene vinyl acetate (EVA) is 24:1 to 49:1.
4 . A method for manufacturing a reduction gear for electric power steering comprising:
adding a first reduction gear composition for electric power steering comprising 95 to 97 parts by weight of polyamide 66 (PA66) among polyamide-based materials and a second reduction gear composition for electric power steering comprising 3 to 5 parts by weight of an ethylene-methacrylic acid copolymer (EMAA) among polyolefin-based materials to a heater having a melting temperature of 250° C. to 260° C. for 2 to 3 minutes, to prepare a mix composition comprising the polyamide 66 (PA66) and the ethylene-methacrylic acid copolymer (EMAA) in a weight ratio of 24:1 to 49:1;
injecting a material comprising the mix composition using an injector at 270° C. to 280° C.; and
cooling the injected material comprising the mix composition at room temperature.
5 . A method for manufacturing a reduction gear for electric power steering comprising:
adding a first reduction gear composition for electric power steering comprising 95 to 97 parts by weight of polyamide 66 (PA66) among polyamide-based materials and a third reduction gear composition for electric power steering comprising 3 to 5 parts by weight of linear low-density polyethylene (LLDPE) among polyolefin-based materials to a heater having a melting temperature of 250° C. to 260° C. for 2 to 3 minutes, to prepare a mix composition comprising the polyamide 66 (PA66) and the linear low-density polyethylene (LLDPE) in a weight ratio of 24:1 to 49:1;
injecting a material comprising the mix composition using an injector at 270° C. to 280° C.; and
cooling the injected material comprising the mix composition at room temperature.
6 . A method for manufacturing a reduction gear for electric power steering comprising:
adding a first reduction gear composition for electric power steering comprising 95 to 97 parts by weight of polyamide 66 (PA66) among polyamide-based materials and a fourth reduction gear composition for electric power steering comprising 3 to 5 parts by weight of ethylene vinyl acetate (EVA) among polyolefin-based materials to a heater having a melting temperature of 250° C. to 260° C. for 2 to 3 minutes, to prepare a mix composition comprising the polyamide 66 (PA66) and the ethylene vinyl acetate (EVA) in a weight ratio of 24:1 to 49:1;
injecting a material comprising the mix composition using an injector at 270° C. to 280° C.;
and cooling the injected material comprising the mix composition at room temperature.