Method of manufacturing reverse osmosis membrane, and reverse osmosis membrane manufactured thereby
There are provided a method of manufacturing a reverse osmosis membrane and a reverse osmosis membrane manufactured thereby. The method includes forming a polysulfone layer by applying a solution including a mixed solvent containing two or more solvents having different solubility parameter values to a surface of a porous support; and forming an active layer on the polysulfone layer.
1. A method of manufacturing a reverse osmosis membrane, the method comprising:
forming a polysulfone layer by applying a solution including a polymer having a sulfonic acid group and a mixed solvent containing two or more solvents having different solubility parameter values to a surface of a porous support, wherein the mixed solvent includes N,N-dimethylformamide (DMF) and dimethyl sulfoxide (DMSO) mixed in a ratio of 90:10 to 60:40, or N,N-dimethylformamide (DMF) and γ-butyrolactone (GBL) mixed in a ratio of 90:10 to 60:40; and
forming an active polyamide layer on the polysulfone layer;
wherein for the same percentage of polysulfone the number of pores that are 0.40 nm or greater is in the range of 0.20% to 0.45%.
2. The method of claim 1 , wherein the solution comprises:
the polymer having a sulfonic acid group in an amount of 5 to 45 parts by weight, based on 100 parts by weight of the solution; and
the mixed solvent containing two or more solvents having different solubility parameter values in an amount of 55 to 95 parts by weight, based on 100 parts by weight of the solution.