Stabilized water-based latex emulsion using chelated metal oxides for fast drying paints
View Patent ↗A shelf-stable fast-cure aqueous coating is disclosed. The coating contains an anionically stabilized latex, a polyfunctional amine and a volatile base that also allows for a chelated metal oxide such that an amount sufficient to deprotonate the conjugate acid of the amine is provided.
1. A fast-cure aqueous coating composition comprising;
(a) an anionically stabilized emulsion polymer having a Tg greater than about 0 degree Centigrade;
(b) a water soluble polyfunctional amine polymer having from about 20% to about 100% of the monomer units by weight containing an amine group and having no acid groups other than trace amounts; and
(c) an amount of volatile base sufficient to raise the pH of the composition to a point where essentially all of the polyfunctional amine is in a non-ionic state; and
(d) at least 1% by weight of an inorganic metal oxide that is either chelated zinc oxide or chelated titanium dioxide or both.
2. The composition of claim 1 wherein the amount of polyfunctional amine is from about 0.25 to about 10 parts per 100 parts emulsion solids by weight.
3. The composition of claim 2 wherein the amount of polyfunctional amine is from about 0.4 to about 5 parts per 100 parts emulsion solids by weight.
4. The composition of claim 3 wherein the amount of polyfunctional amine is from about 0.6 to about 2.5 parts per 100 parts emulsion solids by weight.
5. The coming composition of claim 1 wherein the polyfunctional amine is polyoxazolidinoethylmethacrylate.
6. The coating composition of claim 1 wherein the polyfunctional amine polymer contains dimethylaminopropylmethacrylamide.
7. The coming composition of claim 1 wherein the polyfunctional amine polymer contains oxazolidinoethylmethacrylate.
8. The coating composition of claim 1 wherein the polyfunctional amine polymer contains dimethylaminoethylmethacrylate.
9. A pH stable fast-drying aqueous traffic paint comprising;
(a) an anionically stabilized emulsion polymer having a Tg greater than about 0 degrees Centigrade;
(b) a water soluble polyfunctional amine polymer;
(c) an amount of volatile base sufficient to raise the pH of the composition to a point where essentially all of the polyfunctional amine is in a non-ionic state and wherein chelated zinc oxide or chelated titanium dioxide or both chelated metal oxides are chelated with said amine or chelated with one or more of sodium hydroxide, ammonium hydroxide, or an amino acid.
10. The composition of claim 9 wherein said polyfunctional amine is polymerized from 20% to 100% by weight of amine containing monomer units.
11. The composition of claim 10 wherein said monomer units are selected from the group consisting of dimethylaminopropylmethacrylamide, oxazolidinoethylmethacrylate and dimethylaminoethylmethacrylate.
12. An exterior fast-drying aqueous paint composition comprising;
(a) an anionically stabilized emulsion polymer having a Tg greater than about 0 degrees Centigrade;
(b) 0.6 to 2.5 parts per 100 parts of emulsion solids by weight of a water soluble polyfunctional amine polymer having no acid groups other than trace amounts and polymerized from oxazolidinoethylmethacrylate monomer units; and
(c) an amount of a volatile base sufficient to raise the pH of the composition to a point where essentially all of said polyfunctional amine is in a non-ionic state;
(d) an amount of either chelated zinc oxide or chelated titanium dioxide or both wherein the metal oxide is chelated with an amine or ammonia or hydroxide containing substance.
13. A pH stable fast-drying aqueous traffic paint composition comprising:
(a) an anionically stabilized emulsion polymer having a Tg greater than about 0 degrees Centigrade;
(b) a water soluble polyfunctional amine;
(c) an amount of a volatile base sufficient to raise the pH of the composition to a point where essentially all of said polyfunctional amine is in a non-ionic state;
and;
(d) an amount of either chelated zinc oxide or chelated titanium dioxide or both wherein the metal oxide is chelated with an amine or ammonia or hydroxide containing substance.
14. The composition of claim 13 wherein said polyfunctional amine is polymerized from 20% to 100% by weight of amine containing monomer units.
15. The composition of claim 14 wherein said monomer units are selected from the group consisting of dimethylaminopropylmethacrylamide, oxazolidinoethylmethacrylate and dimethylaminoethylmethacrylate.
16. An exterior pH-stable fast-drying aqueous traffic paint composition comprising:
(a) an anionically stabilized emulsion polymer having a Tg greater than about 0 degrees Centigrade;
(b) 0.6 to 2.5 parts per 100 parts of emulsion solids by weight of a water soluble polyfunctional amine polymer polymerized from oxazolidinoethylmethacrylate monomer units;
(c) an amount of a volatile base sufficient to raise the pH of the composition to a point where essentially all of said polyfunctional amine is in a non-ionic state; and
(d) an amount of either chelated zinc oxide or chelated titanium dioxide or both wherein the metal oxide is chelated with an amine or ammonia or hydroxide containing substance.
17. The composition of claim 16 , wherein said emulsion polymer has a Tg of 20 degrees Centigrade.
18. The composition of claim 16 , wherein the amount of said polyfunctional amine is 1.25 parts per 100 parts of emulsion solids.