View Patent ↗A process for devulcanizing EPDM rubber comprising the step of introducing sulfur-cured EPDM to an extruder, introducing from about 0.5 to about 20 wt % scavenging agent, based upon the total weight of the EPDM and scavenging agent, and mixing and masticating the EPDM at a temperature sufficient to at least partially devulcanize the sulfur-cured EPDM.
1. A process for devulcanizing EPDM rubber comprising the steps of:
introducing sulfur-cured EPDM to an extruder;
introducing from about 0.5 to about 20 wt % of a sulfur scavenging agent to the extruder, based upon the total weight of the EPDM and the sulfur scavenging agent, wherein the sulfur scavenging agent is introduced so as to scavenge sulfur to protect against degradation of the extruder; and
mixing and masticating the EPDM within the extruder in the presence of the sulfur scavenging agent at a temperature sufficient to at least partially devulcanize the sulfur-cured EPDM.
2. The process of claim 1 , further comprising the step of removing volatiles from the extruder.
3. The process of claim 2 , where the volatiles are removed from a vent.
4. The process of claim 2 , where said step of introducing includes introducing from about 1.0 to about 10 wt % of the sulfur scavenging agent, based upon the total weight of the EPDM and the sulfur scavenging agent.
5. The process of claim 1 , where said step of introducing includes introducing from about 1.5 to about 5 wt % of the sulfur scavenging agent, based upon the total weight of the EPDM and the sulfur scavenging agent.
6. The process of claim 5 , wherein the sulfur scavenging agent includes an oxide or a carbonate of an alkali metal or alkaline earth metal.
7. The process of claim 1 , wherein a desiccant is added to the extruder.
8. The process of claim 5 , wherein the desiccant includes an oxide or a carbonate of an alkali metal or alkaline earth metal.