Anode active material for lithium secondary battery and preparation thereof
View Patent ↗The present invention relates to an anode active material for a lithium secondary battery, comprising a carbon material, and a coating layer formed on the surface of particles of the carbon material and having a plurality of Sn-based domains having an average diameter of 1 μm or less. The inventive anode active material having a Sn-based domains coating layer on the surface of a carbon material can surprisingly prevent stress due to volume expansion which generates by an alloy of Sn and lithium. Also, the inventive method for preparing an anode active material can easily control the thickness of the coating layer.
1. An anode active material for a lithium secondary battery, comprising:
a carbon material selected from the group consisting of spherical natural graphite, spherical artificial graphite and a mixture thereof; and
a coating layer consisting of a plurality of Sn-based domains having an average diameter of 1 μm or less,
wherein the coating layer is formed on the surface of particles of the carbon material;
the domains have a hemisphere shape and/or agglomeration of several hemispheres; and
the Sn-based domains are of an Sn alloy and wherein the Sn alloy is an alloy of Sn and a metal selected from the group consisting of Ca, Ti, Cr, Mn, Fe, Co, Ni, Cu, Zn, Ga, Ge, Zr, Nb, Pd, Cd, Sb, Hg, and Bi,
the carbon material has an average particle size of 5 to 100 μm and
the coating layer is formed by electroplating using a pulse current and an electroplating electrolyte wherein the carbon material is dispersed in the electroplating electrolyte, and the coating layer has a density of 2.2 to 5.9 g·cm −3 .
2. The anode active material for a lithium secondary battery according to claim 1 , wherein the carbon material has a specific surface area of 10 m 2 /g or less.
3. An anode of a lithium secondary battery, comprising a current collector; and an anode active material layer formed on at least one surface of the current collector,
wherein the anode active material layer comprises the anode active material according to claim 1 .
4. A lithium secondary battery, comprising a cathode, an anode, and a separator interposed between the cathode and the anode,
wherein the anode is the anode according to claim 3 .