Tissue morphology produced with the fungus
Methods are provided for producing the following tissue characteristics via environmental and chemical manipulation of the vegetative and fruiting phases of the Basidiomycete fungus Pycnoporus cinnabarinus: 1) Aerial vegetative mycelium pigmented with cinnabarinic acid; 2) Aerial vegetative mycelium without pigmentation; 3) A resupinate fruiting body pore surface pigmented with cinnabarinic acid; and 4) Thickened masses of vegetative aerial mycelium.
1. A method comprising the steps of
inoculating a substrate of discrete particles of lignocellulose with Pycnoporus cinnabarinus spawn;
placing the inoculated lignocellulose in an environment consisting of CO 2 above 2%, a relative humidity above 95%, a temperature of from 50° F. to 90° F.; and
incubating the inoculated lignocellulose substrate for a time sufficient to fully colonize said substrate with P. cinnabarinus thereby forming a network of interconnected mycelia cells of P. cinnabarinus extending through and around said discrete particles of lignocellulose to bond said discrete particles together into a self-supporting structure thereof.
2. A method as set forth in claim 1 further comprising the steps of exposing the inoculated lignocellulose in said environment to indirect light and incubating for a period of time sufficient for a pigmented aerial vegetative mycelium to be produced on an external surface of said self-supporting structure.
3. A method as set forth in claim 2 wherein said environment has a CO 2 content of 5% and a relative humidity of 99%.
4. A method as set forth in claim 2 further comprising the step of adding copper to said substrate to increase laccase expression and stimulate pigmentation.
5. A method as set forth in claim 1 further comprising adjusting said environment to consist of CO 2 below 2% and a relative humidity below 95%, exposing the inoculated lignocellulose in said environment to indirect light, and incubating for a period of time sufficient to develop a pigmented resupinate fruiting body pore surface on an external surface of said self-supporting structure.
6. A method as set forth in claim 1 further comprising incubating for a period of time sufficient to develop a surface with thickened masses of vegetative aerial mycelium on an external surface of said self-supporting structure.
7. A method as set forth in claim 6 wherein said period of time is from 3 to 20 days.
8. A method as set forth in claim 6 wherein said thickened masses of vegetative aerial mycelium protrude outwardly from said surface to form a cushioned surface.