Perpendicular magnetic recording medium and method of manufacturing perpendicular magnetic recording medium
A perpendicular magnetic recording medium 100 having a magnetic recording layer 122 , wherein a particle diameter of crystal grains in layer 122 improves a SNR while a high coercive force is maintained. There also is at least a ground layer 118 , a first magnetic recording layer 122 a , and a second magnetic recording layer 122 b in this order on a disk base 110 . The first layer 122 a and the second layer 122 b are ferromagnetic layers, each having a granular structure in which a grain boundary part made of a non-magnetic substance is formed between crystal grains each grown in a columnar shape, and A<B when an average particle diameter of the crystal grains in the first magnetic recording layer 122 a is taken as A nm and an average particle diameter of the crystal grains in the second magnetic recording layer 122 b is taken as B nm.
1. A method of manufacturing a perpendicular magnetic recording medium including at least a ground layer, a non-magnetic granular layer, a first magnetic recording layer, and a second magnetic recording layer in this order on a base, comprising:
forming the first magnetic recording layer using a magnetic target that includes, in a composition, any of chrome, oxygen, or an oxide, or a plurality of oxides, and a gas pressure of approximately 0.5 Pa and a power of approximately 100 to approximately 700 W are set, thereby forming a ferromagnetic layer of a granular structure in which non-magnetic grain boundary parts are formed each between crystal grains each grown in a columnar shape,
forming the second magnetic recording layer using a magnetic target that includes, in a composition, any of chrome, oxygen, or an oxide, or a plurality of oxides, and where a gas pressure of approximately 0.5 Pa and a power of approximately 100 to approximately 1000 W are set, wherein the second magnetic recording layer is a ferromagnetic layer of a granular structure in which non-magnetic grain boundary parts are formed each between crystal grains each grown in a columnar shape, and
wherein A<B when an average particle diameter of the crystal grains in the first magnetic recording layer is taken as A nm and an average particle diameter of the crystal grains in the second magnetic recording layer is taken as B nm, and
the average particle diameter of the non-magnetic granular layer is smaller than the average particle diameter of the first magnetic recording layer.
2. The method of manufacturing a perpendicular magnetic recording medium according to claim 1 , wherein
a ratio between the average particle diameter of the crystal grains in the first magnetic recording layer and the average particle diameter of the crystal grains in the second magnetic recording layer is 0.8<A/B<1.
3. The method of manufacturing a perpendicular magnetic recording medium according to claim 1 , wherein
a total thickness of the first magnetic recording layer and the second magnetic recording layer is equal to or smaller than 15 nm.
4. The method of manufacturing a perpendicular magnetic recording medium according to claim 1 , wherein a non-magnetic substance in which a grain boundary part can be formed includes any of chrome, oxygen, or an oxide, or a plurality thereof.
5. The method of manufacturing a perpendicular magnetic recording medium according to claim 4 , wherein
the oxide includes one or a plurality of oxides selected from the group of SiO 2 , TiO 2 , Cr 2 O 3 , Ta 2 O 5 , Nb 2 O 5 , B 2 O 3 , and ZrO 2 .
6. The method of manufacturing a perpendicular magnetic recording medium according to claim 4 , wherein
an oxide included in the second magnetic recording layer includes one or a plurality of oxides selected from the group of SiO 2 , TiO 2 , Cr 2 O 3 , Ta 2 O 5 , Nb 2 O 5 , B 2 O 3 , and ZrO 2 .
7. The method of manufacturing a perpendicular magnetic recording medium according to claim 2 , wherein
a total thickness of the first magnetic recording layer and the second magnetic recording layer is equal to or smaller than 15 nm.
8. The method of manufacturing a perpendicular magnetic recording medium according to claim 2 , wherein a non-magnetic substance in which a grain boundary part can be formed includes any of chrome, oxygen, or an oxide, or a plurality thereof.
9. The method of manufacturing a perpendicular magnetic recording medium according to claim 3 , wherein a non-magnetic substance in which a grain boundary part can be formed includes any of chrome, oxygen, or an oxide, or a plurality thereof.
10. The method of manufacturing a perpendicular magnetic recording medium according to claim 8 wherein
the oxide includes one or a plurality of oxides selected from the group of SiO 2 , TiO 2 , Cr 2 O 3 , Ta 2 O 5 , Nb 2 O 5 , B 2 O 3 , and ZrO 2 .
11. The method of manufacturing a perpendicular magnetic recording medium according to claim 9 , wherein
the oxide includes one or a plurality of oxides selected from the group of SiO 2 , TiO 2 , Cr 2 O 3 , Ta 2 O 5 , Nb 2 O 5 , B 2 O 3 , and ZrO 2 .
12. The method of manufacturing a perpendicular magnetic recording medium according to claim 8 , wherein
an oxide included in the second magnetic recording layer includes one or a plurality of oxides selected from the group of SiO 2 , TiO 2 , Cr 2 O 3 , Ta 2 O 5 , Nb 2 O 5 , B 2 O 3 , and ZrO 2 .
13. The method of manufacturing a perpendicular magnetic recording medium according to claim 9 , wherein
an oxide included in the second magnetic recording layer includes one or a plurality of oxides selected from the group of SiO 2 , TiO 2 , Cr 2 O 3 , Ta 2 O 5 , Nb 2 O 5 , B 2 O 3 , and ZrO 2 .
14. The method of manufacturing a perpendicular magnetic recording medium according to claim 1 wherein the non-magnetic granular layer includes non-magnetic crystal grains made of a Co alloy and a grain boundary part that comprises at least one of SiOx, Cr, CrO 2 , TiO 2 , ZrO 2 and Ta 2 O 5 .
15. A method of manufacturing a perpendicular magnetic recording medium including at least a ground layer, a first magnetic recording layer, a second magnetic recording layer, and at least a third magnetic recording layer, said layers being provided in this order on a base, comprising:
forming the first magnetic recording layer, the second magnetic recording layer and the at least a third magnetic recording layer as ferromagnetic layers of a granular structure in which grain boundary parts made of a non-magnetic substance are each formed between crystal grains each grown in a columnar shape, and the average particle diameter of the magnetic particles of an upper magnetic recording layer selected from the at least one third magnetic layer, relative to the base side is larger than the average particle diameter of the magnetic particles of a lower magnetic recording layer selected from only one but not the other of the first and second magnetic layers, relative to the upper magnetic recording layer.
16. A method of manufacturing a perpendicular magnetic recording medium including at least a ground layer, a first magnetic recording layer, a second magnetic recording layer, and at least a third magnetic recording layer, said layers being provided in this order on a base, comprising:
forming the first magnetic recording layer, the second magnetic recording layer and the at least a third magnetic recording layer as ferromagnetic layers of a granular structure in which grain boundary parts made of a non-magnetic substance are each formed between crystal grains each grown in a columnar shape,
wherein A<B when an average particle diameter of the crystal grains in the first magnetic recording layer is taken as A nm and an average particle diameter of the crystal grains in the second magnetic recording layer is taken as B nm, and
wherein the average particle diameter of the magnetic particles of an upper magnetic recording layer selected from the second and third magnetic layers, relative to the base side is larger than the average particle diameter of the magnetic particles of a lower magnetic recording layer selected from the first and second magnetic layers, relative to the upper magnetic recording layer, and
forming a non-magnetic granular layer between the ground layer and the first magnetic recording layer, the non-magnetic granular layer having an average particle diameter smaller than the average particle diameter of the first magnetic recording layer.
17. The method according to claim 16 wherein the non-magnetic granular layer includes non-magnetic crystal grains made of a Co alloy and a grain boundary part that comprises at least one of SiOx, Cr, CrO 2 , TiO 2 , ZrO 2 and Ta 2 O 5 .
18. The method according to claim 17 wherein the non-magnetic granular layer comprises Co, Cr, SiO 2 and at least one of Ru, Rh, Pd, Ag, Os, Ir and Au.