Group III nitride crystal production method and group III nitride crystal
View Patent ↗Provided is a high-quality Group III nitride crystal of excellent processability. A Group III nitride crystal is produced by forming a film is composed of an oxide, hydroxide and/or oxyhydroxide containing a Group III element by heat-treating a Group III nitride single crystal at 1000° C. or above, and removing the film.
1. A Group III nitride crystal, comprising a part,
wherein Δd/d(ave) is 4×10 −5 or less, and
Δd/d(ave) is defined as follows:
Δ d/d (ave)=[ d (max)− d (min)]/d(ave),
where d(max), d(min) and d(ave) are respectively maximum, minimum and average values of lattice spacing of (30-30) plane, as measured at 100 μm intervals over a length of 3.5 mm along a c-axis direction.
2. The Group III nitride crystal according to claim 1 , wherein
Δd/d(ave) is 3×10 −5 or less.
3. The Group III nitride crystal according to claim 2 , wherein
Δd/d(ave) is 2×10 −5 or less.
4. The Group III nitride crystal according to claim 1 ,
wherein a direction of crystal growth is a c-axis direction.
5. The Group III nitride crystal according to claim 1 ,
wherein the Group III nitride crystal comprises GaN.
6. A Group III nitride substrate, comprising the Group III nitride crystal according to claim 1 .