Powder resin layered nonwoven material and method of construction thereof

1. A method of constructing a powder resin layered nonwoven material without air pressure or vacuum pressure, comprising:

forming a nonwoven web having opposite first and second sides;

applying a first layer of powder resin material on the first side of an uncoated first portion of the nonwoven web to form a first coated portion of the nonwoven web;

cross-lapping the nonwoven web by reverse-folding an uncoated second portion of the nonwoven web over the first coated portion to sandwich the first layer of powder resin material between the coated first portion and the uncoated second portion;

applying a second layer of powder resin material on the second side of the uncoated second portion to form a second coated portion; and

cross-lapping the nonwoven web by reverse-folding an uncoated third portion of the nonwoven web over the second coated portion to sandwich the second layer of powder resin material between the coated second portion and the uncoated third portion.

2. The method of claim 1 further including applying the powder resin material to the nonwoven web while cross-lapping the nonwoven web.

3. The method of claim 1 further including regulating the amount of powder resin material applied to the nonwoven web.

4. The method of claim 1 further including forming the nonwoven web having a weight between about 0.1 g/sqyd/layer to 15 g/sqyd/layer prior to applying the powder resin material on the web.

5. The method of claim 4 further including forming the nonwoven web having a thickness between about 1-2 mm/layer prior to applying the powder resin material on the nonwoven web and prior to cross-lapping the nonwoven web.

6. A powder resin layered nonwoven material, comprising:

a nonwoven web;

a powder resin material applied on said nonwoven web, said powder resin material forming powder resin layers on opposite sides of said nonwoven web, said nonwoven web not having air pressure or vacuum pressure impregnated powder resin material therein; and

wherein said nonwoven web has a plurality of reverse folds forming overlying layers with said powder resin layers forming separate powder resin layers sandwiched between each of said overlying layers such that said separate powder resin layers are spaced from one another by said overlying layers, wherein said overlying layers are substantially free from air pressure or vacuum pressure impregnated powder resin material.

7. The powder resin layered nonwoven material of claim 6 wherein said nonwoven web has a weight between about 0.1 g/sqyd/layer to 15 g/sqyd/layer.

8. The powder resin layered nonwoven material of claim 7 wherein a single layer of said nonwoven web has a thickness between about 1-2 mm/layer.