Hybrid metallization on plastic for a light emitting diode (LED) lighting system

1. A multi-layer reflective coating for application to a lighting housing assembly, comprising:

an aluminum adhesion promotion layer applied atop a polymer base coat layer, wherein the aluminum adhesion promotion layer comprises a 1-10 nanometer (nm) thick Aluminum (Al) film;

a diffusive barrier layer applied atop the aluminum adhesion promotion layer, wherein the diffusive barrier layer comprises a 50-100 nm thick film of NiCr or Ni and Cr;

a reflective layer applied atop the diffusive barrier layer, wherein the reflective layer comprises 100-400 nm thick silver (Ag) film;

wherein the aluminum adhesion promotion layer promotes adhesion between the polymer base coat layer and the reflective layer; and

a spectrum tunable layer applied atop the reflective layer for spectrum tuning the reflective layer to be used with a light emitting diode lighting source.

2. The multi-layer reflective coating of claim 1 , further comprising a polymer substrate layer below the polymer base coat layer, wherein the polymer substrate layer comprises a ultra-violet cured polyimide that can be applied to plastic, glass or metal.

3. The multi-layer reflective coating of claim 1 , wherein the diffusive barrier layer is applied atop the aluminum adhesion promotion layer for preventing the formation of an Al2Ag alloy due to the migration of atoms from the aluminum adhesion layer with atoms from the silver film of the reflective layer.

4. The multi-layer reflective coating of claim 1 , wherein the spectrum tunable layer comprises a 100-300 nm metal oxide based film.

5. The multi-layer reflective coating of claim 4 , wherein the metal oxide based film is selected from a group comprising Titanium Oxide (TiO2), Silicon Dioxide (SiO2) or Tantalum Pentoxide (Ta2O5) or combination of these metal oxide films.

6. The multi-layer reflective coating of claim 1 , wherein a protective top layer comprising a transparent organic or inorganic-organic hybrid coating is applied atop the spectrum turntable layer as well as the combined previous layers as a protective coating.

7. A method of creating a multi-layer reflective coating, the method comprising:

applying an aluminum adhesion promotion layer atop a polymer base coat layer, wherein the aluminum adhesion promotion layer comprises a 1-10 nanometer (nm) thick Aluminum (Al) film,

applying a diffusive barrier layer atop the aluminum adhesion promotion layer,

wherein the diffusive barrier layer comprises a 50-100 nm thick film of NiCr or Ni and Cr;

applying a reflective layer applied atop the diffusive barrier layer, wherein the reflective layer comprises 200-400 nm thick Silver (Ag) film;

wherein the aluminum adhesion promotion layer promotes adhesion between the polymer base coat layer and the reflective layer; and

applying a spectrum tunable layer atop the reflective layer for spectrum tuning the reflective layer to be used with a Light Emitting Diode lighting source.

8. The method of creating a multi-layer reflective coating of claim 7 , further comprising a polymer substrate layer below the polymer base coat layer, wherein the polymer substrate layer comprises a ultra-violet cured polyimide that can be applied to plastic, glass or metal.

9. The method of creating a multi-layer reflective coating of claim 7 , wherein the diffusive barrier layer is applied atop the aluminum adhesion promotion layer for preventing the formation of an Al2Ag alloy due to the migration of atoms from the aluminum adhesion layer with silver atoms forming the reflective layer.

10. The method of creating a multi-layer reflective coating of claim 7 , wherein the spectrum tunable layer comprises a 100-300 nm thick metal oxide based film, the metal oxide based film is selected from a group comprising Titanium Oxide (TiO2), Silicon Dioxide (SiO2) or Tantalum Pentoxide (Ta2O5) or combination of these metal oxide films.

11. The method of creating a multi-layer reflective coating of claim 7 , wherein the spectrum tunable layer comprises a 100-300 nm thick silicon nitride, or any other kind of nitride, fluoride, or sulfide, or combination of these metal oxide films.

12. The method of creating a multi-layer reflective coating of claim 10 or 11 , wherein the spectrum tunable layer serves also as protective layer for the silver reflective layer.

13. The method of creating a multi-layer reflective coating of claim 7 , wherein a protective top layer comprising a transparent organic or inorganic-organic hybrid coating is applied atop the spectrum turntable layer as well as the combined previous layers as a protective coating.

14. A method of creating a multi-layer reflective coating for a light emitting diode housing assembly, the method comprising:

vacuum coating an aluminum adhesion promotion layer atop a polymer base coat layer, wherein the aluminum adhesion promotion layer comprises a 1-10 nanometer (nm) thick Aluminum (Al) film;

vacuum coating a diffusive barrier layer atop the aluminum adhesion promotion layer,

wherein the diffusive barrier layer comprises a 50-100 nm thick film of NiCr or Ni and Cr;

using vacuum deposition to deposit a silver reflective layer atop the diffusive barrier layer, wherein the silver reflective layer comprises 200-400 nm thick Silver (Ag) film;

wherein the aluminum adhesion promotion layer promotes adhesion between the polymer base coat layer and a silver reflective layer; and

wherein the diffusive barrier layer is applied atop the aluminum adhesion promotion layer for preventing the formation of an Al2Ag alloy due to the migration of atoms between the aluminum adhesion layer and the silver reflective layer; and

vacuum coating a spectrum tunable layer applied atop the silver reflective layer for spectrum tuning the silver reflective layer to be used with a Light Emitting Diode lighting source.