Ti—Al-based alloy ingot having ductility at room temperature
View Patent ↗There is provided a Ti—Al-based alloy ingot having ductility at room temperature, in which the Ti—Al-based ingot has a lamellar structure in which α 2 phases and γ phases are arranged sequentially and regularly, and a thickness ratio γ/α 2 of the γ phase to the α 2 phase is equal to or more than 2. There is also provided a Ti—Al-based alloy ingot having ductility at room temperature, in which the Ti—Al-based alloy ingot has a lamellar structure in which α 2 phases and γ phases are arranged sequentially and regularly, the γ phase has a thickness of 100 nm to 200 nm, and the α 2 phase has a thickness of 100 nm or less.
1. A Ti—Al-based alloy ingot having ductility at room temperature, wherein the Ti—Al-based ingot has a lamellar structure in which α 2 phases and γ phases are arranged sequentially and regularly, and a thickness ratio γ/α 2 of the γ phase to the α 2 phase is equal to or more than 2, and
wherein the Ti—Al-based alloy ingot includes 46 at % of aluminum (Al), 6 at % of niobium (Nb), 0.5 at % of tungsten (W), 0.5 at % of chromium (Cr), 0.3 at % of silicon (Si), 0.1 at % of carbon (C), and titanium (Ti) as a remainder, wherein the Ti—Al-based alloy ingot has a tensile strength of 640 MPa or more.
2. The Ti—Al-based alloy ingot of claim of claim 1 , wherein the γ phase has a thickness of 100 nm to 200 nm.
3. The Ti—Al-based alloy ingot of claim of claim 1 , wherein the α 2 phase has a thickness of 100 nm or less.
4. A Ti—Al-based alloy ingot having ductility at room temperature, wherein the Ti—Al-based alloy ingot has a lamellar structure in which α 2 phases and γ phases are arranged sequentially and regularly, the γ phase has a thickness of 100 nm to 200 nm, and the α 2 phase has a thickness of 100 nm or less, and
wherein the Ti—Al-based alloy ingot includes 44 at % of aluminum (Al), 6 at % of niobium (Nb), 0.5 at % of tungsten (W), 0.5 at % of chromium (Cr), 0.3 at % of silicon (Si), 0.1 at % of carbon (C), and titanium (Ti) as a remainder, wherein the Ti—Al-based alloy ingot has a tensile strength of 640 MPa or more.
5. A Ti—Al-based alloy ingot having ductility at room temperature in a casting state prior to a subsequent heat treatment, wherein the Ti—Al-based ingot has a lamellar structure in which α 2 phases and γ phases are arranged sequentially and regularly, a thickness ratio γ/α 2 of the γ phase to the α 2 phase is equal to or more than 2, and
wherein the Ti—Al-based alloy ingot includes 44-46 at % of aluminum (Al), 6 at % of niobium (Nb), 0.5 at % of tungsten (W), 0.5 at % of chromium (Cr), 0.3 at % of silicon (Si), 0.1 at % of carbon (C), and titanium (Ti) as a remainder, wherein the Ti—Al-based alloy ingot has a tensile strength of 640 MPa or more.
6. The Ti—Al-based alloy ingot of claim 5 , wherein the γ phase has a thickness of 100 nm to 200 nm.
7. The Ti—Al-based alloy ingot of claim 5 , wherein the Ti—Al-based alloy ingot has a yield stress of 590 MPa or more.
8. The Ti—Al-based alloy ingot of claim 5 , wherein the Ti—Al-based alloy ingot has a strain of 0.384% or more.