Methods for reducing asphalt pavement thickness
View Patent ↗Methods for reducing asphalt pavement thickness are provided. A method for producing thin asphalt pavement includes combining a base asphalt, an oxidized polyolefin, and an aggregate to form an asphalt paving material. A layer of the asphalt paving material is deposited on a substrate layer and compacted to a thickness.
1. A method for producing thin asphalt pavement, the method comprising the steps of:
combining a base asphalt, an oxidized polyolefin, and an aggregate to form an asphalt paving material;
establishing, at a predetermined thickness, a high temperature rutting measurement of a comparative compacted asphalt paving material comprising the aggregate and the base asphalt with no oxidized polyolefin; and
depositing a layer of the asphalt paving material on a substrate layer and compacting the asphalt paving material to a thickness that is less than the predetermined thickness of the comparative compacted asphalt paving material while achieving the same amount or less of high temperature rutting than the high temperature rutting measurement of the comparative compacted asphalt paving material.
2. The method of claim 1 , wherein the oxidized polyolefin has a molecular weight of from about 1000 to about 30,000 Daltons.
3. The method of claim 1 , wherein the oxidized polyolefin comprises oxidized polyethylene.
4. The method of claim 3 , wherein the oxidized polyolefin is an oxidized polyethylene homopolymer.
5. The method of claim 4 , wherein the oxidized polyethylene homopolymer is an oxidized high density polyethylene homopolymer having a density in the range of about 0.93 to about 1 g/cc.
6. The method of claim 4 , wherein combining comprises mixing the base asphalt with the oxidized polyethylene homopolymer to form an asphalt binder with the oxidized polyethylene homopolymer present in an amount of about 0.25 to about 10 wt. % based on a total weight of the asphalt binder.
7. The method of claim 6 , wherein combining comprises mixing the base asphalt with the oxidized polyethylene homopolymer to form an asphalt binder with the oxidized polyethylene homopolymer present in an amount of about 1 to about 4 wt. % based on a total weight of the asphalt binder.
8. The method of claim 4 , wherein combining comprises mixing the base asphalt with the oxidized polyethylene homopolymer to form an asphalt binder with the oxidized polyethylene homopolymer present in an amount of about 0.5 to about 2 wt. % and SBS present in an amount of about 2 wt. % SBS based on a total weight of the asphalt binder.
9. The method of claim 1 , wherein combining comprises mixing the base asphalt with the oxidized polyolefin to form an asphalt binder that comprises substantially no anti-stripping agent.
10. The method of claim 1 , wherein depositing comprises depositing the layer of the asphalt paving material on the substrate layer and compacting to a thickness that is less than a thickness of the comparative compacted asphalt paving material while achieving less than 25% alligator cracking.