Synthesis of 2,3,3,3-tetrafluoropropene/vinylidene fluoride copolymers
View Patent ↗In accordance with the present invention, aqueous emulsion polymerization processes of synthesizing 2,3,3,3-tetrafluoropropene/vinylidene fluoride copolymers having 2,3,3,3-tetrafluoropropene as the major monomer unit are provided.
1. A process of synthesizing a copolymer consisting essentially of 2,3,3,3-tetrafluoro-propene/vinylidene fluoride, said copolymer having 2,3,3,3-tetrafluoropropene as a major monomer unit,
the process consisting essentially of the step of conducting an aqueous emulsion copolymerization of monomers in the presence of a water soluble radical initiator to form the 2,3,3,3-tetrafluoropropene/vinylidene fluoride copolymer having 2,3,3,3-tetrafluoro-propene as the major monomer unit, wherein the copolymerization is carried out at a temperature from 55° C. to 70° C., for from about 12 to about 100 hours,
wherein the total weight of the radical initiator added is less than 1 wt % based on the weight of all the monomers in the copolymerization;
wherein the water soluble radical initiator is added into the copolymerization at least two separated times during the reaction process; and
wherein the water soluble radical initiator is added into the copolymerization at two different copolymerization temperatures, a first temperature below 0° C. and a second temperature above 0° C.
2. The process of claim 1 , wherein the monomers are 2,3,3,3-tetrafluoropropene and vinylidene fluoride.
3. The process of claim 1 , wherein the 2,3,3,3-tetrafluoro-propene/vinylidene fluoride copolymer having 2,3,3,3-tetrafluoropropene as the major monomer unit has a monomer unit ratio of 2,3,3,3-tetrafluoro-propene/vinylidene fluoride between 80/20 mol % and 99/1 mol %.
4. The process of claim 1 , wherein the water soluble radical initiator is selected from the group consisting of Na 2 S 2 O 8 , K 2 S 2 O 8 , (NH 4 ) 2 S 2 O 8 , Fe 2 (S 2 O 8 ) 3 , K 2 S 2 O 8 /FeSO 4 , and (NH 4 ) 2 S 2 O 8 /FeSO 4 .
5. The process of claim 1 , wherein the water soluble radical initiator is added into the copolymerization at two or three different separated times.
6. A process of synthesizing a copolymer consisting essentially of 2,3,3,3-tetrafluoro-propene/vinylidene fluoride, said copolymer having 2,3,3,3-tetrafluoropropene as a major monomer unit,
the process consisting essentially of the step of conducting an aqueous emulsion copolymerization of monomers in the presence of a water soluble radical initiator to form the 2,3,3,3-tetrafluoropropene/vinylidene fluoride copolymer having 2,3,3,3-tetrafluoro-propene as the major monomer unit, wherein the copolymerization is carried out at a temperature from 55° C. to 70° C., for from about 12 to about 100 hours,
wherein the total weight of the radical initiator added is less than 1 wt % based on the weight of all the monomers in the copolymerization;
wherein the water soluble radical initiator is added into the copolymerization at least two separated times during the reaction process; and
wherein the water soluble radical initiator is added into the copolymerization at two different copolymerization temperatures, a first temperature of about −4° C. and a second temperature of from about 55 to 60° C.