Polarizing plate, method for preparing the same, and optical display apparatus including the same

1. A polarizing plate, comprising:

a polarizer, a half-wavelength (λ/2) retardation film, and a quarter-wavelength (λ/4) retardation film,

wherein an absolute orthogonal b-coordinate value based on a CIELAB color coordinate system is approximately 3 or less when the polarizing plate is stacked with a reference polarizing plate having a degree of polarization of at least 99.9% such that an angle between an absorption axis of the polarizer and a reference absorption axis of a reference polarizer of the reference polarizing plate is 90°,

wherein at a wavelength of 550 nanometers, the quarter-wavelength (λ/4) retardation film has an out-of-plane retardation value ranging from approximately −100 nanometers to approximately −130 nanometers, and

wherein the out-of-plane retardation value (Rth) is calculated using the formula Rth=((nx+ny)/2−nz)×d, wherein nx, ny, and nz are refractive indexes in x-, y-, and z-axis directions of each retardation film, and d is a thickness of the retardation film.

2. The polarizing plate according to claim 1 , wherein the polarizing plate comprises the polarizer, a protective film formed on an upper side of the polarizer, the λ/2 retardation film formed on a lower side of the polarizer, and the λ/4 retardation film formed on a lower side of the λ/2 retardation film.

3. The polarizing plate according to claim 1 , wherein the absolute orthogonal b-coordinate value ranges from approximately 1.9 to approximately 2.6.

4. The polarizing plate according to claim 1 , wherein the polarizing plate has a moisture content ranging from approximately 2.0 wt % to approximately 3 wt %, and the polarizer has a boric acid content ranging from approximately 20.5 wt % to approximately 22.5 wt %.

5. The polarizing plate according to claim 4 , wherein the polarizer has a thickness ranging from approximately 5 micrometers to approximately 25 micrometers.

6. The polarizing plate according to claim 2 , wherein the protective film comprises a resin comprising cellulose, polyester, cyclic polyolefin, polycarbonate, polyether sulfone, polysulfone, polyamide, polyimide, polyolefin, polyarylate, polyvinyl alcohol, polyvinyl chloride, and/or polyvinylidene chloride.

7. The polarizing plate according to claim 1 , wherein at a wavelength of 550 nanometers, the half-wavelength (λ/2) retardation film has an in-plane retardation value ranging from approximately 200 nanometers to approximately 300 nanometers, and the quarter-wavelength (λ/4) retardation film has an in-plane retardation value ranging from approximately 100 nanometers to approximately 200 nanometers.

8. The polarizing plate according to claim 1 , wherein at a wavelength of 550 nanometers, the half-wavelength (λ/2) retardation film has an out-of-plane retardation value ranging from approximately 220 nanometers to approximately 240 nanometers.

9. The polarizing plate according to claim 1 , wherein the half-wavelength (λ/2) retardation film comprises a cycloolefin film, and the quarter-wavelength (λ/4) retardation film comprises an acrylic film.

10. The polarizing plate according to claim 1 , wherein the half-wavelength (λ/2) retardation film and the quarter-wavelength (λ/4) retardation film comprise birefringences of opposite signs.

11. The polarizing plate according to claim 1 , further comprising a protective film between the polarizer and the half-wavelength (λ/2) retardation film, or between the half-wavelength (λ/2) retardation film and the quarter-wavelength (λ/4) retardation film.

12. A method for preparing a polarizing plate, comprising:

preparing a polarizer comprising approximately 25 wt % to approximately 26 wt % moisture and approximately 20.5 wt % to approximately 22.5 wt % boric acid; and

forming a protective film and/or a retardation film on at least one surface of the polarizer,

wherein preparing the polarizer comprises:

stretching a polyvinyl alcohol film in an aqueous boric acid solution comprising approximately 3.0 wt % to approximately 3.5 wt % boric acid, and

drying the stretched polyvinyl alcohol film at a drying temperature of approximately 50° C. to approximately 70° C., and at an air volume having an air supply rate of approximately 1400 RPM to approximately 1500 RPM, and an air exhaust rate of approximately 2000 RPM to approximately 3000 RPM.

13. The method according to claim 12 , wherein forming the protective film and/or the retardation film comprises:

placing a protective film on an upper surface of the polarizer, and

placing a half-wavelength (λ/2) retardation film on a lower surface of the polarizer, and a quarter-wavelength (λ/4) retardation film on a lower surface of the half-wavelength (λ/2) retardation film.

14. An optical display apparatus comprising:

a panel; and

a polarizing plate stacked on an upper surface of the panel;

wherein the polarizing plate comprises a polarizer having an absorption axis, a half-wavelength (λ/2) retardation film on a lower surface of the polarizer, and a quarter-wavelength (λ/4) retardation film on a lower surface of the half-wavelength (λ/2) retardation film,

wherein an absolute orthogonal b-coordinate value based on a CIELAB color coordinate system is approximately 3 or less when the polarizing plate is stacked with a reference polarizing plate having a degree of polarization of at least 99.9% such that an angle between the absorption axis of the polarizer and a reference absorption axis of a reference polarizer of the reference polarizing plate is 90°,

wherein at a wavelength of 550 nanometers, the quarter-wavelength (λ/4) retardation film has an out-of-plane retardation value ranging from approximately −100 nanometers to approximately −130 nanometers, and

wherein the out-of-plane retardation value (Rth) is calculated using the formula Rth=((nx+ny)/2−nz)×d, wherein nx, ny, and nz are refractive indexes in x-, y-, and z-axis directions of each retardation film, and d is a thickness of the retardation film.

15. The optical display apparatus according to claim 14 , wherein the polarizer further comprises a transmission axis, and the absolute orthogonal b-coordinate value based on the CIELAB color coordinate system is approximately 3 or less when the polarizing plate is stacked with the reference polarizing plate having a degree of polarization of at least 99.9% such that an angle between the transmission axis of the polarizer and a reference transmission axis of the reference polarizer of the reference polarizing plate is 90°.

16. The optical display apparatus according to claim 14 , wherein the apparatus is an organic light emitting diode (OLED) display apparatus.

17. The optical display apparatus according to claim 14 , wherein the polarizing plate further comprises:

a protective film on an upper surface of the polarizer; and

an adhesive layer on a lower surface of the half-wavelength (λ/2) retardation film.

18. The optical display apparatus according to claim 17 , wherein the polarizing plate further comprises a second adhesive layer on a lower surface of the a quarter-wavelength (λ/4) retardation film.

19. The optical display apparatus according to claim 14 , wherein:

the polarizing plate has a moisture content ranging from approximately 2.0 wt % to approximately 2.8 wt %;

the polarizer has a boric acid content ranging from approximately 20.5 wt % to approximately 22.5 wt %; and

the half-wavelength (λ/2) retardation film has an in-plane retardation value ranging from approximately 200 nanometers to approximately 300 nanometers, and the quarter-wavelength (λ/4) retardation film has an in-plane retardation value ranging from approximately 100 nanometers to approximately 200 nanometers at a wavelength of 550 nanometers; and

the half-wavelength (λ/2) retardation film has an out-of-plane retardation value ranging from approximately 220 nanometers to approximately 240 nanometers at a wavelength of 550 nanometers.