Flash control metal bonding

1. A method of bonding together first and second metal plates comprising:

supporting said first plate atop a corresponding mold;

positioning said second plate atop said first plate, with a thermosetting adhesive therebetween to form a lap joint;

vacuum bagging said second plate atop said first plate, with a porous peel ply applied directly atop both said first and second plates in a bridge therebetween covering said lap joint and a porous breather ply covering said peel ply;

applying a vacuum through said breather ply to clamp said second plate atop said first plate;

thermally curing said adhesive to bond said second plate to said first plate at said lap joint, with said breather and peel plies being preselected to capture adhesive seepage from said lap joint during said curing to correspondingly reduce cured adhesive flash exposed on said first plate; and

removing said breather and peel plies from atop said first and second plates and removing therewith said captured adhesive seepage.

2. A method according to claim 1 wherein:

said second plate terminates at a step atop said first plate to expose said adhesive at said joint;

said peel ply conforms with said step adjacent to said adhesive in said joint; and

said peel ply is preselected in porosity for locally channeling to said breather ply said adhesive seepage along said step during said curing.

3. A method according to claim 2 further comprising:

placing said mold and vacuum bagged first and second plates in an autoclave;

curing said adhesive under heat and pressure in said autoclave for effecting viscous seepage thereof from said joint; and

preselecting said peel ply in combination with said adhesive, breather ply, curing temperature, and curing pressure for promoting said viscous adhesive seepage through said peel ply into said breather ply.

4. A method according to claim 3 wherein said peel ply is preselected to replace an otherwise required deflashing post-operation following thermal curing of said adhesive in a metal bonding method for said first and second plates using a different peel ply.

5. A method according to claim 3 further comprising:

applying a masking flashbreaker tape atop said first plate along said step adjacent to said exposed adhesive;

applying said peel ply directly atop said flashbreaker tape in said step and extending laterally oppositely directly atop both said first and second plates;

curing said adhesive for channeling said seepage both atop said flashbreaker tape and through said peel ply at said step; and

removing said breather and peel plies and said captured adhesive seepage, and additionally removing said flashbreaker tape to tear flash thereon from said joint.

6. A method according to claim 3 wherein said peel ply is selected from a plurality of different pre-existing peel plies commercially available from a plurality of different manufacturers.

7. A method according to claim 3 further comprising:

adhesively bonding together said first and second plates in an original bonding method including an original peel ply to produce an initial bonded assembly;

measuring size of flash atop said first plate along said step in said initial bonded assembly;

revising said bonding method for a second set of said first and second plates to include at least one method difference in said vacuum bagging process and thermal curing;

adhesively bonding together said second set of first and second plates using said revised bonding method to produce a second bonded assembly;

measuring size of flash atop said first plate along said step in said second bonded assembly; and

revising sequentially said difference in sequential bonding methods to produce corresponding bonded assemblies until measured flash in said revised bonding method is less than measured flash in a previous bonding method.

8. A method according to claim 7 wherein said bonding method difference includes replacing said original peel ply with a different peel ply having different characteristics.

9. A method according to claim 8 wherein only said peel ply difference is revised in said sequential bonding methods.

10. A method according to claim 8 further comprising:

applying an original flashbreaker tape atop said first plate along said step adjacent to said exposed adhesive in said original bonding method for masking said first plate from said flash; and

said bonding method difference additionally includes replacing said original flashbreaker tape with a different flashbreaker tape having different characteristics.

11. A method according to claim 10 wherein only said peel ply and flashbreaker tape differences are revised in said sequential bonding methods.

12. A method according to claim 3 wherein said vacuum bagging comprises:

applying a single peel ply directly atop said first and second plates to conform with said step;

applying a single breather ply directly atop said single peel ply;

applying a vacuum bag sealingly joined around a perimeter thereof to said first plate to cover said breather and peel plies and said second plate; and

said first and second plates are imperforate at said lap joint, with said thermosetting adhesive therein being exposed solely along said step for locally seeping through said peel ply at said step.

13. A method according to claim 3 wherein said peel ply is further preselected for tear resistance with said captured adhesive seepage to avoid tearing thereof upon removal of said breather and peel plies after said thermal curing of said adhesive.

14. A method according to claim 3 further comprising cleaning and priming said first and second metal plates prior to applying said thermosetting adhesive in said lap joint.

15. A method according to claim 3 wherein:

said first and second metal plates comprise aluminum;

said preselected breather ply comprises non-woven polyester fibers in a weight species of about 339 g/m 2 ;

said preselected peel ply is selected from the group consisting of woven nylon fabric in a thickness of about 0.152 mm and weight species of about 75 g/m 2 ; and open-weave woven nylon fabric in a thickness of about 0.114 mm and weight species of about 75 g/m 2 ; and

said adhesive comprises a thermosetting epoxy structural adhesive film in a weight species of about 293 g/m 2 and a predetermined thermal and pressure curing cycle.

16. A method of bonding first and second metal plates with a thermosetting adhesive at a lap joint to reduce cured adhesive flash thereat comprising:

bridging said metal plates at said lap joint with a porous ply applied directly atop both said first and second plates in a bridge therebetween, with said porous ply being preselected to capture adhesive seepage from said lap joint;

vacuum bagging said metal plates and porous ply to clamp together said metal plates under vacuum;

thermally curing said adhesive for promoting viscous adhesive seepage into said porous ply; and

removing said porous ply from said lap joint and removing therewith said captured adhesive seepage.

17. A method according to claim 16 wherein said porous ply is preselected in combination with said adhesive and curing temperature and pressure thereof for promoting said viscous adhesive seepage.

18. A method according to claim 17 further comprising:

adhesively vacuum bonding together said metal plates in an original bonding method;

measuring flash at said lap joint; and

revising said vacuum bonding method sequentially with at least one corresponding method difference, and measuring flash at said lap joint until measured flash in said revised vacuum bonding method is less than measured flash in a previous vacuum bonding method.

19. A method according to claim 18 further comprising bridging said lap joint first with a porous peel ply covered in turn by a porous breather ply, with said peel ply being preselected in porosity for locally channeling to said breather ply said adhesive seepage, and said breather ply being preselected to capture said adhesive seepage.