Ceramic honeycomb structure and its production method
A ceramic honeycomb structure having a large number of flow paths partitioned by porous cell walls, the cell walls meeting the conditions; (a) the cell walls having porosity of 55-80%, (b) the cell walls having a median pore diameter D50 (measured by mercury porosimetry) of 5-27 μm, (c) pores open on cell wall surfaces having an opening area ratio of 20% or more, (d) pores open on cell wall surfaces having a median opening diameter d50 (determined from equivalent circle diameters on an area basis) of 10-45 μm, (e) the density of pores open on cell wall surfaces having equivalent circle diameters of 10 μm or more and less than 40 μm being 350/mm 2 or more, (f) the maximum inclination of a curve of a cumulative pore volume relative to a pore diameter (determined from a pore distribution measured by mercury porosimetry) being 1.6 or more, and (g) a ratio D50/d50 of the median pore diameter D50 to the median opening diameter d50 being 0.65 or less.
1. A method for producing a ceramic honeycomb structure, comprising the steps of extrusion-molding a moldable material containing a ceramic material and a pore-forming material to obtain a predetermined molding, and drying and sintering said molding; said moldable material containing 2-20% by mass of said pore-forming material based on 100% by mass of said ceramic material; said pore-foaming material having a median diameter of 5-70 μm; and said pore-forming material being hollow resin particles having inorganic powder on their outer surfaces, wherein said pore-forming material is produced by bringing said inorganic powder into contact with said resin particles wet with water.
2. The method for producing a ceramic honeycomb structure according to claim 1 , wherein said inorganic powder is at least one selected from the group consisting of kaolin, silica, talc, cordierite, alumina, aluminum hydroxide, calcium carbonate and titanium oxide.
3. The method for producing a ceramic honeycomb structure according to claim 1 , wherein said inorganic powder has a median diameter of 0.5-15 μm.
4. The method for producing a ceramic honeycomb structure according to claim 1 , wherein said ceramic material is a cordierite-forming material, wherein said cordierite-forming material contains 15-25% of silica, and wherein said silica having a median diameter of 20-30 μm and sphericity of 0.5 or more.
5. The method for producing a ceramic honeycomb structure according to claim 4 , wherein said cordierite-forming material contains talc having a median diameter of 1-10 μm.
6. A method for producing a ceramic honeycomb structure, comprising the steps of extrusion-molding a moldable material containing a ceramic material and a pore-forming material to obtain a predetermined molding, and drying and sintering said molding; said ceramic material being a cordierite-forming material; said cordierite-forming material containing 15-25% of silica; said silica having a median diameter of 20-28 μm and sphericity of 0.5 or more; said moldable material containing 2-20% by mass of said pore-forming material based on 100% by mass of said ceramic material; said pore-forming material having a median diameter of 5-70 μm; and said pore-forming material being solid or hollow resin particles having inorganic powder on their outer surfaces, wherein a ratio (d/D) of a median diameter (d) of said inorganic powder to the median diameter (D) of said resin particles is 0.01-0.5, and wherein said pore-forming material is produced by bringing said inorganic powder into contact with said resin particles wet with water.
7. The method for producing a ceramic honeycomb structure according to claim 1 , wherein said moldable material contains 2-7.5% by mass of said pore-forming material based on 100% by mass of said ceramic material.
8. The method for producing a ceramic honeycomb structure according to claim 6 , wherein said moldable material contains 2-7.5% by mass of said pore-forming material based on 100% by mass of said ceramic material.
9. A method for producing a ceramic honeycomb structure, comprising the steps of extrusion-molding a moldable material containing a ceramic material and a pore-forming material to obtain a predetermined molding, and drying and sintering said molding; said moldable material containing 2-20% by mass of said pore-forming material based on 100% by mass of said ceramic material; said pore-forming material having a median diameter of 5-70 μm; and said pore-forming material being solid resin particles having inorganic powder on their outer surfaces, wherein said pore-forming material is produced by bringing said inorganic powder into contact with said resin particles wet with water.