Active-Energy-Curable Resin Composition, Molding, Microrelief Structure, Water-Repellent Article, Mold, and Method for Producing Microrelief Structure
Disclosed is an active energy ray-curable resin composition comprising 3 to 18 parts by mass of an alkyl (meth)acrylate (A) having an alkyl group of 12 or more carbon atoms, and 82 to 97 parts by mass of a multifunctional monomer (B) having 3 or more radical polymerizable functional groups in the molecule wherein the sp value as expressed by the Fedor's estimation method is 20 to 23, per 100 parts by mass of the total content of all monomers, and which gives a cured material having excellent water repellency and scratch resistance; and a molded article, a fine uneven structure body and a water-repellent article prepared by using the active energy ray-curable resin composition; and a method for producing a fine uneven structure body.
1 . An active energy ray-curable resin composition comprising
3 to 18 parts by mass of an alkyl (meth)acrylate (A) having an alkyl group of 12 or more carbon atoms, and
82 to 97 parts by mass of a multifunctional monomer (B) having 3 or more radical polymerizable functional groups in the molecule wherein the sp value as expressed by the Fedor's estimation method is 20 to 23,
per 100 parts by mass of the total content of all monomers.
2 . The active energy ray-curable resin composition according to claim 1 , which contains no solvent.
3 . The active energy ray-curable resin composition according to claim 1 , which further comprises 0 to 15 parts by mass of a monomer (C) having at least one radical polymerizable functional group per 100 parts by mass of the total content of all monomers.
4 . The active energy ray-curable resin composition according to claim 1 which further comprises a slip agent (D).
5 . A molded article composed of a cured material of the active energy ray-curable resin composition according to claim 1 .
6 . A fine uneven structure body which is a cured material of the active energy ray-curable resin composition according to claim 1 , and has a fine uneven structure on the surface.
7 . A water-repellent article having the fine uneven structure body according to claim 6 .
8 . A method for producing a fine uneven structure body comprising a substrate and a cured material having a fine uneven structure on the surface, comprising
providing the active energy ray-curable resin composition according to claim 1 between the substrate and a mold having an inversion structure of the fine uneven structure,
curing the activation energy ray-curable resin composition by irradiation of an activation energy ray, and
detaching the mold to form a cured material having the fine uneven structure on the surface.
9 . A mold having the fine uneven structure body according to claim 6 .
10 . A method for producing a fine uneven structure body comprising a substrate and a thermoplastic resin layer having a fine uneven structure on the surface, comprising
providing a thermoplastic resin on the substrate,
pressing the mold according to claim 9 onto the thermoplastic resin with heating, and then cooling it, and
detaching the mold to form a cured material having a structure on the surface of the thermoplastic resin layer which corresponds to an inversion structure of the fine concave-convex structure of the mold.
11 . A method for producing a fine uneven structure body comprising a substrate and a cured material having a fine uneven structure on the surface, comprising
providing an active energy ray-curable resin composition between the mold according to claim 9 and the substrate,
curing the activation energy ray-curable resin composition by irradiation of an activation energy ray, and
detaching the mold to form a cured material having a structure on the surface which corresponds to an inversion structure of the fine uneven structure of the mold.
12 . A method for producing a fine uneven structure body comprising a substrate and a cured material having a fine uneven structure on the surface, comprising
transferring the fine uneven structure of the mold according to claim 9 to the active energy ray-curable resin composition, and then detaching the mold, and
curing the active energy ray-curable resin composition to form a cured material having a structure on the surface which corresponds to an inversion structure of the fine uneven structure of the mold.