Extruded 3XXX-series aluminium alloy tube product
View Patent ↗An aluminum alloy extruded tube product for a heat exchanger assembly and made from a 3xxx-series aluminum alloys and including furthermore a purposive addition of one or more wetting elements selected from the group of: Bi 0.03% to 0.5%, Pb 0.03% to 0.5%, Sb 0.03% to 0.5%, Li 0.03% to 0.5%, Se 0.03% to 0.5%, Y 0.03% to 0.05%, Th 0.03% to 0.05%, and the sum of these elements being 0.5% or less.
1. A method of manufacturing an article joined by brazing or an assembly of brazed components, comprising the steps of:
(a) forming the components of which at least one is made from an aluminium alloy extruded tube product made from a 3xxx-series aluminium alloy modified to include a purposive addition of Bi,
said alloy having a composition comprising, in wt. %:
Mn 0.05 to 2.0%,
Mg up to 1%,
Si up to 1.2%,
Fe up to 0.8%,
Cu up to 0.2%,
Zn up to 0.5%,
Ti up to 0.25%,
optionally one or more elements selected from the group consisting of:
Zr 0.03 to 0.3, Cr 0.03 to 0.4, Hf 0.03 to 0.4, and Sc 0.03 to 0.3,
unavoidable impurities and balance aluminium, and
furthermore the purposive addition of Bi in a range of 0.03% to 0.5%,
wherein the aluminium alloy is devoid of Li, Na, K, and Ca,
(b) assembling the components into an assembly,
(c) brazing the assembly without applying brazing flux on the assembly of components and brazing the whole assembly in an inert controlled gas atmosphere at a brazing temperature to form a brazed assembly, and
(d) cooling of the brazed assembly.
2. The method according to claim 1 , wherein the aluminium alloy extruded tube product consists of the 3xxx-series aluminium alloy.
3. The method according to claim 2 , wherein the 3xxx alloy comprises both Bi and Mg, and wherein the excess Mg content with respect to the stoichiometric composition of Bi 2 Mg 3 is 0.1% or less.
4. The method according to claim 1 , wherein the tube 3xxx-series aluminium alloy comprises Ti in a range of 0.2 to 0.25%.
5. The method according to claim 1 , wherein the 3xxx-series aluminium alloy has a composition further comprising, in wt. %:
the one or more elements selected from the group consisting of:
Hf 0.03 to 0.4 and Sc 0.03 to 0.3.
6. The method according to claim 1 , and wherein the 3xxx-series alloy has a composition within the range selected from the group of 3002, 3102, 3003, 3103, 3103A, 3103B, 3004, 3005, and 3105.
7. The method according to claim 1 , wherein the aluminium alloy extruded tube product is a multi-porthole tube.
8. The method according to claim 3 , wherein the 3xxx alloy comprises both Bi and Mg, and wherein the excess Mg content with respect to the stoichiometric composition of Bi 2 Mg 3 is 0.07% or less.
9. The method according to claim 1 , and wherein the aluminium alloy extruded tube comprises purposive addition of Bi in a range of 0.03 to 0.35%.
10. The method according to claim 1 , wherein the aluminium alloy extruded tube product has purposive addition of Bi in a range of 0.03 to 0.30%.
11. The method according to claim 1 , wherein the aluminium alloy extruded tube has 0.06% to 0.5% Bi.
12. The method according to claim 2 , wherein the aluminium alloy extruded tube product 3xxx-series aluminium alloy consists of, in wt. %:
Mn 0.05 to 2.0%,
Mg up to 1%,
Si up to 1.2%,
Fe up to 0.8%,
Cu up to 0.2%,
Zn up to 0.5%,
Ti up to 0.25%,
optionally one or more elements selected from the group consisting of: Zr 0.03 to 0.3, Cr 0.03 to 0.4, Hf 0.03 to 0.4, and Sc 0.03 to 0.3,
unavoidable impurities and balance aluminium,
furthermore the purposive addition of Bi in a range of 0.03% to 0.5%,
wherein the aluminium alloy is devoid of Li, Na, K, and Ca.
13. The method according to claim 1 , wherein the aluminium alloy extruded tube product made from the 3xxx-series aluminium alloy has:
Mn 0.45% to 1.4%,
Si up to 0.5%,
Zn up to 0.3%,
Ti up to 0.2%,
Cr 0.03 to 0.3%,
unavoidable impurities and balance aluminium.
14. The method according to claim 1 , wherein during step (c) the brazing temperature is in the range of 540° C. to 615° C.
15. The method according to claim 1 , wherein during step (c) the oxygen content in the inert controlled gas atmosphere is below 200 ppm.
16. The method according to claim 1 , wherein during step (c) the oxygen content in the inert controlled gas atmosphere is below 100 ppm.
17. The method according to claim 1 , wherein during step (c) the oxygen content in the inert controlled gas atmosphere is less than 15 ppm.
18. The method according to claim 12 , wherein the aluminium alloy extruded tube 3xxx-series aluminium alloy Ti level is 0.2% to 0.25% and the aluminium alloy extruded tube 3xxx-series aluminium alloy contains the one or more elements selected from the group consisting of: Hf 0.03 to 0.4 and Sc 0.03 to 0.3.
19. The method according to claim 2 , wherein the aluminium alloy extruded tube product 3xxx-series aluminium alloy consists of, in wt. %:
Mn 0.05 to 2.0%,
Mg up to 1%,
Si up to 1.2%,
Fe up to 0.8%,
Zn up to 0.5%,
Ti up to 0.25%,
optionally the one or more elements selected from the group consisting of:
Zr 0.03 to 0.3, Cr 0.03 to 0.4, Hf 0.03 to 0.4, and Sc 0.03 to 0.3,
unavoidable impurities and balance aluminium,
furthermore the purposive addition of Bi in a range of 0.03% to 0.5%,
wherein the aluminium alloy is devoid of Li, Na, K, and Ca.
20. The method according to claim 2 , wherein the aluminium alloy extruded tube product 3xxx-series aluminium alloy consists of, in wt. %:
Mn 0.05 to 2.0%,
Mg up to 1%,
Si up to 1.2%,
Fe up to 0.8%,
Zn up to 0.5%,
Ti 0.2 to 0.25%,
one or more elements selected from the group consisting of: Hf 0.03 to 0.4 and Sc 0.03 to 0.3,
optionally one or more elements selected from the group consisting of: Zr 0.03 to 0.3 and Cr 0.03 to 0.4,
unavoidable impurities and balance aluminium,
furthermore the purposive addition of Bi in a range of 0.03% to 0.5%,
wherein the aluminium alloy is devoid of Li, Na, K, and Ca.