Polyurethane foam and method for producing same
View Patent ↗The invention relates to a method for producing a polyurethane foam, wherein a mixture having the following is discharged from a mixing head through a discharge line: A) a component reactive toward isocyanates; B) a surfactant component; C) a blowing agent component selected from the group comprising linear, branched, or cyclic C1 to C6 hydrocarbons, linear, branched, or cyclic C1 to C6 fluorocarbons, N2, O2, argon, and/or CO2, wherein the blowing agent C) is present in the supercritical or near-critical state; and D) a polyisocyanate component. The component A) has a hydroxyl value=100 mg KOH/g and =1000 mg KOH/g. The blowing agent component C) is present at least partially in the form of an emulsion, and means provided with an opening or several openings are arranged in the discharge line in order to increase the flow resistance during the discharge of the mixture comprising A), B), C), and D), wherein the cross-sectional area of the opening or the sum of the cross-sectional areas of all openings is =0.1% and =99.9% of the inner cross-sectional area of the discharge line.
1. A method of producing a polyurethane foam comprising the steps of:
providing a mixture in a high-pressure mixing head, said mixture comprising:
A) an isocyanate-reactive component;
B) a surfactant component;
C) a blowing agent component selected from the group consisting of a linear C 1 to C 6 hydrocarbon, a branched C 1 to C 6 hydrocarbon, a cyclic C 1 to C 6 hydrocarbon, a linear C 1 to C 6 fluorocarbon, a linear C 1 to C 6 hydrofluorocarbon, a branched C 1 to C 6 fluorocarbon, a branched C 1 to C 6 hydrofluorocarbon, a cyclic C 1 to C 6 fluorocarbon, a cyclic C 1 to C 6 hydrofluorocarbon, N 2 , O 2 , argon, and CO 2 , wherein said blowing agent C) is in the supercritical or near-critical state; and
D) a polyisocyanate component;
discharging the mixture comprising A), B), C) and D) from the mixing head through a discharge line, wherein a pressure of ≧80 bar to ≦150 bar prevails in the mixing head after the step of providing the mixture,
wherein said isocyanate-reactive component A) has a hydroxyl number of ≧100 mg KOH/g to ≦1000 mg KOH/g,
said blowing agent component C) is at least partly present in the form of an emulsion, wherein the proportion of blowing agent component C) is ≧4% to ≦40% by weight based on the overall weight of the mixture, and
one or more apertures are disposed in the discharge line to elevate the flow resistance during the step of discharging the mixture comprising A), B), C) and D), wherein the one or more apertures comprises a cross-sectional area, wherein the cross-sectional area of the one or more apertures or the sum total of a single cross-sectional area of each of said one or more apertures amounts to ≧0.1% to ≦99.9% of the inner cross-sectional area of the discharge line.
2. The method as claimed in claim 1 wherein the cross-sectional area of the one or more apertures or the sum total of a single cross-sectional area of each of said one or more apertures amounts to ≧0.5% to ≦10% of the inner cross-sectional area of the discharge line.
3. The method as claimed in claim 1 wherein the ratio of the volume of a reaction chamber which is inside and/or outside the mixing head to the cross-sectional area of the one or more apertures or to the sum total of the cross- sectional areas of all apertures is ≧5 m to ≦200 m.
4. The method as claimed in claim 1 wherein the step of discharging the mixture comprising A), B), C) and D) from the mixing head is effected such that the ratio of the volume flow of the mixture to the cross-sectional area of the one or more apertures or to the sum total of the cross-sectional areas is >5 m/s to <400 m/s.
5. The method as claimed in claim 1 wherein the mixture in the mixing head has a residence time ≧0 seconds to ≦20 seconds.
6. The method as claimed in claim 1 wherein said isocyanate-reactive component A) comprises a polyetherester polyol having a hydroxyl number of ≧200 mg KOH/g to ≦600 mg KOH/g and a short-chain polyol having a hydroxyl number of ≧800 mg KOH/g.
7. The method as claimed in claim 1 wherein said surfactant component B) comprises a polysiloxane-polyoxyalkylene copolymer.
8. The method as claimed in claim 1 wherein the proportion of blowing agent component C) is ≧4% by weight to ≦12% by weight, based on the overall weight of the mixture.
9. The method as claimed in claim 1 wherein said polyisocyanate component D) comprises monomeric and/or polymeric diphenylmethane 4,4′-diisocyanate.
10. A polyurethane foam obtained by the method of claim 1 .
11. The polyurethane foam as claimed in claim 10 with an apparent density of ≧20 kg/m 3 to ≦160 kg/m 3 .
12. The method as claimed in claim 1 , wherein said isocyanate-reactive component A) comprises a polyetherester polyol having a hydroxyl number of ≧200 mg KOH/g to ≦600 mg KOH/g and a short-chain polyol having a hydroxyl number of ≧800 mg KOH/g, and wherein the polyurethane foam has an apparent density of 30 kg/m 3 to ≦120 kg/m 3 .
13. The method as claimed in claim 12 , wherein the proportion of blowing agent component C) is >7% by weight to <9% by weight, based on the overall weight of the mixture.
14. The method as claimed in claim 1 wherein the mixture in the mixing head has a residence time ≧0.5 seconds to ≦5 seconds.