Optical coupling device having KBBF group crystal coupled with prisms and method for manufacturing same

1. A KBBF family nonlinear optical crystal-prism coupler, comprising: a KBBF family crystal with two smooth surfaces; transition layers each of which is deposited on respective one of the two smooth surfaces of the KBBF family crystal; and two prisms each of which optically contacts with respective one of the activated transition layers, wherein the transition layers are in thickness of 200 nm-1000 nm, and the materials of the transition layers and the prisms can be identical or different; the smooth surfaces of the KBBF family crystal are crystallographic c-plane; each of the smooth surfaces of the KBBF family crystal has a roughness of Ra less than 0.5 nm and a surface flatness less than ⅛ λ (λ=632.8 nm); and the KBBF family crystal is a single KBBF family crystal or a combination of several layers of KBBF family crystals, which are combined by optical contact through the transition layers, the transition layers are coatings of different materials from that of the KBBF family crystal.

2. The KBBF family nonlinear optical crystal-prism coupler according to claim 1 , wherein the KBBF family crystal is KBe 2 BO 3 F 2 crystal, RbBe 2 BO 3 F 2 crystal or CsBe 2 BO 3 F 2 crystal.

3. The KBBF family nonlinear optical crystal-prism coupler according to claim 1 , wherein the prisms are made of optical crystal or optical glass.

4. The KBBF family nonlinear optical crystal-prism coupler according to claim 3 , wherein the optical crystal prisms are made of calcium fluoride and the optical glass prisms are made of fused silica glass.

5. The KBBF family nonlinear optical crystal-prism coupler according to claim 1 , wherein the transition layers are formed of calcium fluoride or silicon dioxide.

6. A fabrication method for the KBBF family nonlinear optical crystal-prism coupler according to claim 1 , comprising the steps of:

processing two optical contact surfaces of a KBBF family crystal and optical contact surfaces of two prisms by fine polishing so that each of the fine-polished surfaces of the KBBF family crystal and the prisms has a roughness of Ra less than 0.5 nm and a surface flatness less than ⅛ λ (λ=632.8 nm);

depositing the transition layers on both the fine-polished surfaces of the KBBF family crystal, in which the transition layers are in thickness of 200 nm-1000 nm and the materials of the transition layers and the prisms can be identical or different;

activating the transition layers of the KBBF family crystal; and

bonding the transition layers deposited on the KBBF family crystal and the optical contact surfaces of the prisms by optical contact and then heating the bonded crystal-prism coupler at an elevated temperature to ensure that the crystal and the prisms are bonded to each other firmly, thereby achieving the KBBF family nonlinear optical crystal-prism coupler,

wherein the heating process is performed under 50-600° C. for 1-120 hours, the atmosphere of the heat treatment can be in air, inert, reducing or oxidizing gas.

7. The fabrication method according to claim 6 , wherein the KBBF family crystal is KBe 2 BO 3 F 2 crystal, RbBe 2 BO 3 F 2 crystal or CsBe 2 BO 3 F 2 crystal.

8. The fabrication method according to claim 6 , wherein the prisms are made of optical crystal or optical glass.

9. The fabrication method according to claim 8 , wherein the optical crystal prisms are made of calcium fluoride and the optical glass prisms are made of fused silica glass.

10. The fabrication method according to claim 6 , wherein the depositing process is chemical vapor deposition, physical vapor deposition or sputter deposition.

11. The fabrication method according to claim 6 , wherein the activating process is plasma activation or mechanical polishing activation.

12. A KBBF family nonlinear optical crystal-prism coupler, comprising:

a KBBF family crystal with two smooth surfaces;

a pair of prisms each of which has a smooth surface;

first transition layers each of which is deposited on respective one of the two smooth surfaces of the KBBF family crystal; and

second transition layers each of which is deposited on a smooth surface of respective one of the pair of prisms, wherein

the first transition layers deposited on both the smooth surfaces of the KBBF family crystal are optically bonded with the second transition layers deposited on both the smooth surfaces of the two prisms;

the first and second transition layers are in thickness of 200 nm-1000 nm, the materials of the first and second transition layers and the KBBF family crystal are of different materials of the same type of optical substances, and the materials of the first and second transition layers and the prisms can be identical or different;

the smooth surfaces of the KBBF family crystal are crystallographic c-plane;

each of the smooth surfaces of the KBBF family crystal and the prisms has a roughness of Ra less than 0.5 nm and a surface flatness less than ⅛ λ (λ=632.8 nm); and

the KBBF family crystal is a single KBBF family crystal or a combination of several layers of KBBF family crystals, which are combined by optical contact through the transition layers, the transition layers are coatings of different material from that of the KBBF family crystal.

13. The KBBF family nonlinear optical crystal-prism coupler according to claim 12 , wherein the first and second transition layers are formed of calcium fluoride or silicon dioxide.

14. A fabrication method for the KBBF family nonlinear optical crystal-prism coupler according to claim 12 , comprising the steps of:

processing two optical contact surfaces of a KBBF family crystal and optical contact surfaces of two prisms by fine polishing so that each of the fine-polished surfaces of the KBBF family crystal and the prisms has a roughness of Ra less than 0.5 nm and a surface flatness less than ⅛ λ (λ=632.8 nm);

depositing each of the first transition layers on respective one of the fine-polished surfaces of the KBBF family crystal and each of the second transition layers on respective one of the fine-polished surfaces of the prisms, in which the first and second transition layers are in thickness of 200 nm-1000 nm, the materials of the first and second transition layers and the KBBF family crystal are of different materials of the same type of optical substances, and the materials of the first and second transition Layers and the prisms can be identical or different;

activating the first and second transition layers; and

bonding one of the first transition layers deposited on the KBBF family crystal and the second transition layer of the respective prism by optical contact, bonding the other first transition layer and the second transition layer of the other prism by optical contact, and then heating the bonded crystal-prism coupler at an elevated temperature to ensure that the crystal and the prisms are bonded to each other firmly, thereby achieving the KBBF family nonlinear optical crystal-prism coupler,

wherein the heating process is performed under 50-600° C. for 1-120 hours, the atmosphere of the heat treatment can be in air, inert, reducing or oxidizing gas.

15. The fabrication method according to claim 14 , wherein the first and second transition layers are formed of calcium fluoride or fused silica.

16. The fabrication method according to claim 14 , wherein the KBBF family crystal is KBe 2 BO 3 F 2 crystal, RbBe 2 BO 3 F 2 crystal or CsBe 2 BO 3 F 2 crystal.

17. The fabrication method according to claim 14 , wherein the prisms are made of optical crystal or optical glass.

18. The fabrication method according to claim 17 , wherein the optical crystal prisms are made of calcium fluoride and the optical glass prisms are made of fused silica glass.

19. The fabrication method according to claim 14 , wherein the depositing process is chemical vapor deposition, physical vapor deposition or sputter deposition.

20. The fabrication method according to claim 14 , wherein the activating process is plasma activation or mechanical polishing activation.

21. The KBBF family nonlinear optical crystal-prism coupler according to claim 12 , wherein the KBBF family crystal is KBe 2 BO 3 F 2 crystal, RbBe 2 BO 3 F 2 crystal or CsBe 2 BO 3 F 2 crystal.

22. The KBBF family nonlinear optical crystal-prism coupler according to claim 12 , wherein the prisms are made of optical crystal or optical glass.

23. The KBBF family nonlinear optical crystal-prism coupler according to claim 22 , wherein the optical crystal prisms are made of calcium fluoride and the optical glass prisms are made of fused silica glass.