View Patent ↗The present invention concerns a method for the treatment of stimulable phosphors and/or screens for use in diagnosis, in particular medical radiography. The method comprises subjecting the stimulable phosphors and/or screens to an epoxide containing gaseous compound, promptly following their manufacture. By applying the method according to the invention yellowing of the stimulable phosphors and/or screens is prevented in a safe and efficient manner; thereby the disadvantages known as such resulting from such yellowing will not occur.
1. A method for the production of a phosphorous screen wherein
i) said phosphorous screen comprises a phosphorous composition containing iodine, and
ii) a treatment with at least an epoxy group containing compound in gaseous form is applied to the phosphorous composition of i) during the manufacturing process of the phosphorous screen, wherein
iii) the treatment of ii) is applied in an after-treatment room, autoclave or sterilization room.
2. The method according to claim 1 , wherein the phosphorous composition comprises alkaline earth material halogenide phosphors.
3. The method according to claim 1 , wherein the phosphorous composition further comprises a bariumfluorohalogenide phosphor.
4. The method according to claim 1 , wherein the phosphorous composition also comprises divalent europium as activator.
5. The method according to claim 1 , wherein the epoxy group containing compound is oxirane.
6. The method according to claim 1 , wherein the treatment with at least an epoxy group containing compound is performed to the phosphorous composition before it is applied onto the screen.
7. The method according to claim 1 , wherein the treatment with at least an epoxy group containing compound is performed to the phosphorous composition after said composition is applied to the screen and before the screen is slit and/or cut into desirable formats and shapes.
8. The method according to claim 7 , wherin the phosphorous screen is slit and/or cut into the desirable formats and shapes after the treatment with at least an epoxy group containing compound is performed to the phosphorous composition.
9. The method according to claim 7 , wherein the phosphorous composition is a powder.