Multi-layer coating with cubic boron nitride particles
A physical configuration of multiple-layer coatings formed with at least one layer of coating containing cubic born nitride (cBN) particles with one or more layers in composite form containing cBN particles may have a thickness of each individual layer as thin as in the nanometer range, or as thick as in the range of a few microns and even up to tens of microns. The chemistry of the composite layer consists of any individual phase of (a) nitrides such as titanium nitride (TiN), titanium carbonitride (TiCN), and hafnium nitride (HfN); (b) carbides such as titanium carbide (TiC); and (c) oxides such as aluminum oxide (AI 2 O 3 ) or any combination of the above phases, in addition to cBN particles. The coating or film can be stand-alone or on a substrate.
1. A multi-layer coated substrate, consisting of:
a. a substrate formed of a substrate material chosen from the set consisting of carbides, ceramics, polycrystalline cubic boron nitride (PCBN) compacts, PCBN tips, cermets, carbon, and steels;
b. a composite layer deposited on the substrate, the composite layer consisting of cubic boron nitride (cBN) particles and a second material chosen from the set consisting of nitrides, carbides, carbonitrides, borides, and oxides;
c. a first stacked ceramic layer deposited on the composite layer, the first stacked ceramic layer consisting of a third material chosen from the set consisting of nitrides, carbides, carbonitrides, oxides, or any combination thereof; and
d. a second stacked ceramic layer deposited on the first stacked ceramic layer, the second stacked ceramic layer consisting of a fourth material chosen from the set consisting of nitrides, carbides, carbonitrides, oxides, or any combination thereof, wherein the third material and fourth material are different.
2. The multi-layer coated substrate of claim 1 , wherein the cBN particles in the composite layer make up 20% to 60% of the composite layer.
3. The multi-layer coated substrate of claim 2 , wherein each of the composite layer, first stacked ceramic layer, and second stacked ceramic layer comprise a thickness in the range of 200 nm to 10 μm.