In-situ reactor blend of a Ziegler-Natta catalysed, nucleated polypropylene and a metallocene catalysed polypropylene

1. Propylene homo- or copolymer composition obtained in the presence of a catalyst mixture comprising: a Ziegler-Natta catalyst system and a metallocene catalyst system, the composition comprising an in-situ reactor blend of a Ziegler-Natta catalyzed, nucleated polypropylene (znPP) and a metallocene catalyzed polypropylene (mcPP), in a weight ratio in the range of 6:94 to 50:50 (wt % znPP:wt % mcPP) said propylene homo- or copolymer composition is endowed with the following features:

a) a MFR 2 according to ISO 1133 (230° C., 2.16kg) in the range of 0.01 to 500 g/10min,

b) a comonomer-content (determined with FTIR) in the range of 0.0to 8.0 wt %,

c) xylene cold solubles (XCS) determined at 23 ° C. according to ISO 6427of less than 10.0 wt %,

d) in case of propylene homopolymers with isotactic pentads (mmmm) measured by 13 C-NMR higher than 90%,

e) a melting temperature T m measured by DSC between 135° C. to 170° C.,

f) a crystallization temperature T c measured by DSC between 100° C. to 135° C., and

g) in case of propylene copolymers with a randomness measured by FTIR higher than 95%.

2. Propylene homo- or copolymer composition according to claim 1 having:

a tensile modulus (E) measured according to ISO 527-2 in the range of 500 to 3000 MPa,

a Charpy notched impact strength (NIS) determined according to ISO 179-1eA:2000 at 23° C. in the range of 0.3 to 55 kJ/m 2 and at 0° C. in the range of 0.3to 10 kJ/m 2 , and

haze values according to ASTM D 1003 (1mm placque) in the range of 5 to 55 %.

3. Propylene homo- or copolymer composition according to claim 1 , wherein the composition is either:

a propylene homopolymer composition comprising an in-situ reactor blend of a znPP-homopolymer and a mcPP-homopolymer, or

a propylene copolymer composition comprising an in-situ reactor blend of a znPP-copolymer and a mcPP-copolymer.

4. Propylene homo- or copolymer composition according to claim 1 , wherein the Ziegler-Natta catalyst system for obtaining the Ziegler-Natta catalyzed, nucleated polypropylene comprises:

(a 1 ) a Ziegler-Natta procatalyst,

(a 2 ) a cocatalyst, and

(a 3 ) an external donor,

the Ziegler-Natta catalyst system being modified with a vinyl compound of formula (V) CH 2 ═CH—CHR 7 R 8 , wherein R 7 and R 8 together form a 5- or 6-membered saturated, unsaturated or aromatic ring or independently represent an alkyl group comprising 1 to 4 carbon atoms.

5. Propylene homo- or copolymer composition according to claim 4 , wherein the Ziegler-Natta procatalyst contains a trans-esterification product of a C 1 -C 4 -alcohol and a phthalic ester as internal donor.

6. Propylene homo- or copolymer composition according to claim 5 , wherein the Ziegler-Natta procatalyst is prepared by:

a) reacting a spray crystallized or emulsion solidified adduct of MgCl 2 and a C 1 -C 4 -alcohol with TiCl 4 ;

b) reacting the product of stage a) with a dialkylphthalate of formula (I):

wherein R 1 ′ and R 2 ′ are independently at least a C 5 -alkyl,

under conditions where a transesterification between said C 1 -C 4 -alcohol and said dialkylphthalate of formula (I) takes place to form the internal donor,

c) washing the product of stage b) and

d) optionally reacting the product of step c) with additional TiCl 4 .

7. Propylene homo- or copolymer composition according to claim 4 , wherein the used external donor is represented by formula (III) and/or (IV)

Si(OCH 2 CH 3 ) 3 (NR 3 R 4 )  (III)

R 5 n R 6 m Si(OR 7 ) z   (IV)

wherein R 3 and R 4 can be the same or different and represent a hydrocarbon group having 1to 12 carbon atoms and R 5 and R 6 can be the same or different and represent a hydrocarbon group having 1 to 12 carbon atoms, R 7 is methyl or ethyl, z is 2 or 3 with the proviso that n+m+z=4.

8. Propylene homo- or copolymer composition according to claim 4 , wherein the used cocatalyst is selected from trialkylaluminum , dialkyl aluminum chloride and alkyl aluminum sesquichloride.

9. Propylene homo- or copolymer composition according to claim 1 , wherein the metallocene catalyst system for obtaining the metallocene catalyzed polypropylene comprises:

(b 1 ) a metallocene compound of formula (VI)

R n (Cp′) 2 MX 2   (VI)

wherein

“M” is zirconium (Zr) or hafnium (Hf),

each “X” is independently a monovalent anionic σ-ligand,

each “Cp'′” is a cyclopentadienyl-type organic ligand independently selected from the group consisting of substituted cyclopentadienyl, substituted indenyl, substituted tetrahydroindenyl, and substituted or unsubstituted fluorenyl, said organic ligands coordinate to the transition metal (M),

“R” is a bivalent bridging group linking said organic ligands (Cp′), and

“n” is 1 or 2, and

(b 2 ) a cocatalyst.

10. Propylene homo- or copolymer composition according to claim 9 , wherein the cocatalyst is an aluminoxane.

11. Propylene homo- or copolymer composition according to claim 9 , wherein the metallocene catalyst system used is obtained by the emulsion/solidification technology.

12. Propylene homo- or copolymer composition according to claim 11 , wherein the metallocene catalyst system used is obtained by:

a) preparing a solution of one or more catalyst components selected from the metallocene compound (b 1 ) and the cocatalyst (b 2 ) in a solvent;

b) dispersing said solution in a second solvent to form an emulsion in which said one or more catalyst components are present in the droplets of the dispersed phase, and

c) solidifying said dispersed phase to convert said droplets to solid particles and optionally recovering said particles to obtain said catalyst system.

13. A method comprising: using a catalyst mixture comprising:

(a) 5 to 40 wt % of a Ziegler-Natta catalyst system comprising

(a 1 ) a Ziegler-Natta procatalyst,

(a 2 ) a cocatalyst and

(a 3 ) an external donor,

the Ziegler-Natta catalyst system being modified with a vinyl compound of formula (V) CH 2 ═CH—CHR 7 R 8 , wherein R 7 and R 8 together form a 5- or 6-membered saturated, unsaturated or aromatic ring or independently represent an alkyl group comprising 1 to 4 carbon atoms and

(b) 95 to 60 wt % of a metallocene catalyst system comprising

(b 1 ) a metallocene compound of formula (VI)

R n (Cp′) 2 MX 2   (VI)

wherein

“M” is zirconium (Zr) or hafnium (Hf),

each “X” is independently a monovalent anionic σ-ligand,

each “Cp′ ” is a cyclopentadienyl-type organic ligand independently selected from the group consisting of substituted cyclopentadienyl, substituted indenyl, substituted tetrahydroindenyl, and substituted or unsubstituted fluorenyl, said organic ligands coordinate to the transition metal (M),

“R” is a bivalent bridging group linking said organic ligands (Cp′), and

“n” is 1 or 2, and

(b 2 ) a cocatalyst,

for the production of a propylene homo- or copolymer composition being an in-situ reactor blend of a Ziegler-Natta catalysed, nucleated polypropylene (znPP) and a metallocene catalysed polypropylene (mcPP), said propylene homo- or copolymer composition being endowed with the following features:

a) a MFR 2 according to ISO 1133 (230° C., 2.16kg) in the range of 0.01 to 500 g/10min,

b) a comonomer-content (determined with FTIR) in the range of 0.0 to 8.0 wt %,

c) xylene cold solubles (XCS) determined at 23 ° C. according to ISO 6427of less than 10.0 wt %,

d) in case of propylene homopolymers with isotactic pentads (mmmm) measured by 13 C-NMR higher than 90%,

e) a melting temperature T m measured by DSC between 135° C. to 170° C. and,

f) a crystallisation temperature T c measured by DSC between 100° C. to 135° C.,

g) in case of propylene copolymers with a randomness measured by FTIR higher than 95%, wherein the method comprises contacting the catalyst mixture with propylene and an optional additional monomer under copolymerization conditions to form the propylene homo- or copolymer composition.