Treated inorganic pigments having reduced photoactivity and improved anti-microbial properties and their use in coating compositions
View Patent ↗The disclosure provides a coating composition comprising a treated inorganic particle having reduced photoactivity and improved anti-microbial properties, wherein the treated inorganic particle comprises: an inorganic core particle; a first treatment of a silicon compound, wherein the silicon compound is added in a single step; and a second treatment comprising co-precipitated zinc oxide and alumina.
1. A coating composition comprising a treated inorganic particle having reduced photoactivity and improved anti-microbial properties, wherein the treated inorganic particle comprises:
a. an inorganic core particle;
b. a first treatment of a silicon compound encapsulating the inorganic core particle, wherein the silicon compound has been deposited onto the inorganic core particle in a single step; and
c. a second treatment over the first treatment, said second treatment comprising zinc oxide and alumina that has been simultaneously precipitated onto the first treatment.
2. The coating composition of claim 1 further comprising a resin.
3. The coating composition of claim 2 wherein the resin is acrylic, styrene-acrylic, vinyl-acrylic, ethylene-vinyl acetate, vinyl acetate, alkyd, vinyl chloride, styrene-butadiene, vinyl versatate, vinyl acetate-maleate, or a mixture thereof.
4. The coating composition of claim 3 wherein the alkyd resin is a complex branched or cross-linked polyester having unsaturated aliphatic acid residues.
5. The coating composition of claim 1 wherein the resin is a urethane resin.
6. The coating composition of claim 2 wherein the resin is present in the amount of about 5 to about 40% by weight, based on the total weight of the coating composition.
7. The coating composition of claim 1 wherein the inorganic core particle is ZnS, TiO 2 , CaCO 3 , BaSO 4 , ZnO, MoS 2 , silica, talc or clay.
8. The coating composition of claim 7 wherein the inorganic core particle is a titanium dioxide particle.
9. The coating composition of claim 7 wherein the silicon compound is silica.
10. The coating composition of claim 9 wherein the silica is pyrogenically added silica.
11. The coating composition of claim 9 wherein the silica is applied to an inorganic core particle in an aqueous slurry.
12. The coating composition of claim 1 wherein the silicon compound is present in the amount of about 0.5 to about 20% by weight, based on the total weight of the inorganic core particle.
13. The coating composition of claim 1 wherein the alumina is present in the amount of about 0.05% to 20% by weight, calculated as Al 2 O 3 , and based on the total weight of the inorganic core particle.
14. The coating composition of claim 1 wherein the zinc oxide is present in the amount of about 0.3 to about 5% by weight, based on the total weight of the inorganic core particle.
15. The coating composition of claim 8 wherein the titanium dioxide particle has chalk fade of greater than about 20.
16. The coating composition of claim 8 wherein the titanium dioxide particle has an acid solubility of less than about 15.
17. The coating composition of claim 1 wherein the coating composition is a paint.
18. The coating composition of claim 17 wherein the paint is applied to a surface selected from the group consisting of building material, automobile part, sporting good, tenting fabric, tarpaulin, geo membrane, stadium seating, lawn furniture and roofing material.
19. The coating of claim 18 wherein the surface the paint is applied to is a roofing material.
20. A dried coating prepared from a coating composition comprising a treated inorganic pigment, wherein the treated inorganic pigment comprises:
a. an inorganic core particle;
b. a first treatment of a silicon compound encapsulating the inorganic core particle, wherein the silicon compound has been deposited onto the inorganic core particle in a single step; and
c. a second treatment over the first treatment, said second treatment comprising zinc oxide and alumina that has been simultaneously precipitated onto the first treatment.