Cross-linkable silicone composition and cross-linked product thereof

1. A cross-linkable silicone composition comprising at least the following components:

(A) an organopolysiloxane represented by the following average unit formula:

(R 1 3 SiO 1/2 ) a (R 1 2 SiO 2/2 ) b (R 1 SiO 3/2 ) c (SiO 4/2 ) d (R 2 O 1/2 ) e

 where R 1 are phenyl groups, alkyl or cycloalkyl groups having 1 to 6 carbon atoms, or alkenyl groups having 2 to 6 carbon atoms, and where 60 to 80 mole % of R 1 are phenyl groups and 10 to 20 mole % of R 1 are alkenyl groups; R 2 is a hydrogen atom or an alkyl group having 1 to 6 carbon atoms; and “a”, “b”, “c”, “d”, and “e” are numbers that satisfy the following conditions: 0≦a≦0.2; 0.2≦b≦0.7; 0.2≦c≦0.6; 0≦d≦0.2; 0≦e≦0.1; and a+b+c+d=1;

(B) an organopolysiloxane represented by the following general formula:

R 3 3 SiO(R 3 2 SiO) m SiR 3 3

 where R 3 are phenyl groups, alkyl or cycloalkyl groups having 1 to 6 carbon atoms, or alkenyl groups having 2 to 6 carbon atoms, and where 40 to 70 mole % of R 3 are phenyl groups and at least one R 3 is an alkenyl group; and “m” is an integer in the range of 5 to 100, wherein component (B) is used in an amount of 0 to 20 parts by weight per 100 parts by weight of component (A);

(C) an organopolysiloxane having in one molecule two silicon-bonded hydrogen atoms and where phenyl groups constitute 30 to 70 mole % of silicon-bonded organic groups and where the mole ratio of silicon-bonded hydrogen atoms contained in this component to the total sum of alkenyl groups contained in components (A) and (B) is in the range of 0.5 to 2; and

(D) a hydrosilylation catalyst in an amount sufficient to promote a hydrosilylation reaction between the alkenyl groups contained in components (A) and (B) and silicon-bonded hydrogen atoms contained in component (C).

2. The cross-linkable silicone composition according to claim 1 , wherein component (C) is an organopolysiloxane represented by the following general formula:

(HR 4 2 SiO) 2 SiR 4 2

where R 4 designate phenyl groups, or alkyl and cycloalkyl groups having 1 to 6 carbon atoms, and where 30 to 70 mole % of R 4 are phenyl groups.

3. A cross-linked product obtained by subjecting the cross-linkable silicone composition according to claim 2 to a hydrosilylation reaction.

4. The cross-linked product according to claim 3 , wherein the cross-linked product has type A durometer hardness at 25° C. according to JIS K 6253 equal to or greater than 60.

5. The cross-linked product according to claim 3 , wherein the cross-linked product has type A durometer hardness at 100° C. according to JIS K 6253 equal to or lower than 10.

6. A cross-linked product obtained by subjecting the cross-linkable silicone composition according to claim 1 to a hydrosilylation reaction.

7. The cross-linked product according to claim 6 , wherein the cross-linked product has type A durometer hardness at 25° C. according to JIS K 6253 equal to or greater than 60.

8. The cross-linked product according to claim 6 , wherein the cross-linked product has type A durometer hardness at 100° C. according to JIS K 6253 equal to or lower than 10.

9. The cross-linkable silicone composition according to claim 1 , further comprising a reaction inhibitor selected from the group of an alkyne alcohol, an enyne compound, 1,3,5,7-tetramethyl-1,3,5,7-tetravinylcyclotetrasiloxane, 1,3,5,7-tetramethyl-1,3,5,7-tetrahexenylcyclotetrasiloxane, or benzotriazole.

10. The cross-linkable silicone composition according to claim 1 , further comprising an adhesion-imparting agent comprising a linear, branched, or cyclic organosiloxane oligomer having 4 to 20 silicon atoms, or an organosilane.