Carburization resistant metal material
View Patent ↗There is provided a carburization resistant metal material suitable as a raw material for cracking furnaces, reforming furnaces, heating furnaces, heat exchangers, etc. in petroleum and gas refining, chemical plants, and the like. This metal material consists of, by mass %, C: 0.03 to 0.075%, Si: 0.6 to 2.0%, Mn: 0.05 to 2.5%, P: 0.04% or less, S: 0.015% or less, Cr: higher than 16.0% and less than 20.0%, Ni: 20.0% or higher and less than 30.0%, Cu: 0.5 to 10.0%, Al: 0.15% or less, Ti: 0.15% or less, N: 0.005 to 0.20%, and O (oxygen): 0.02% or less, the balance being Fe and impurities. The metal material may further contain one kind or more kinds of Co, Mo, W, Ta, B, V, Zr, Nb, Hf, Mg, Ca, Y, La, Ce and Nd.
1. A metal material, consisting of, by mass %, C: 0.032 to 0.075%, Si: 0.63 to 1.67%, Mn: 0.18 to 1.32%, P: 0.035% or less, S: 0.012% or less, Cr: 16.2 to 19.9%, Ni: 21.7 to 29.6%, Cu: 0.72 to 4.25%, Al: 0.15% or less, Ti: 0.12% or less, N: 0.008 to 0.140%, and O (oxygen): 0.02% or less, the balance being Fe and impurities.
2. The metal material according to claim 1 ,
characterized by having a fine grain size such that the austenite grain size is No. 6 or higher.
3. A metal material, consisting of, by mass %, C: 0.032 to 0.075%, Si: 0.63 to 1.67%, Mn: 0.18 to 1.32%, P: 0.035% or less, S: 0.012% or less, Cr: 16.2 to 19.9%, Ni: 21.7 to 29.6%, Cu: 0.72 to 4.25%, Al: 0.15% or less, Ti: 0.12% or less, N: 0.008 to 0.140%, O (oxygen): 0.02% or less, at least one kind of a component selected from at least one group of the first group to the fifth group described below, and the balance being Fe and impurities:
first group: Co: 10% or less,
second group: Mo: 5% or less, W: 5% or less, and Ta: 5% or less,
third group: B: 0.1% or less, V: 0.5% or less, Zr: 0.5% or less, Nb: 2% or less, and Hf: 0.5% or less,
fourth group: Mg: 0.1% or less and Ca: 0.1% or less,
fifth group: Y: 0.15% or less, La: 0.15% or less, Ce: 0.15% or less, and Nd: 0.15% or less.
4. The metal material according to claim 3 ,
characterized by having a fine grain size such that the austenite grain size is No. 6 or higher.
5. A metal material, consisting of, by mass %, C: 0.04 to 0.07%, Si: 0.8 to 1.5%, Mn: 0.18 to 1.32%, P: 0.035% or less, S: 0.012% or less, Cr: 18.0% to 19.9%, Ni: 22.0 to 28.0%, Cu: 1.5 to 4.25%, Al: 0.12% or less, Ti: 0.05% or less, N: 0.008 to 0.140%, and O (oxygen): 0.02% or less, the balance being Fe and impurities.
6. The metal material according to claim 5 ,
characterized by having a fine grain size such that the austenite grain size is No. 6 or higher.
7. A metal material, consisting of, by mass %, C: 0.04 to 0.07%, Si: 0.8 to 1.5%, Mn: 0.18 to 1.32%, P: 0.035% or less, S: 0.012% or less, Cr: 18.0% to 19.9%, Ni: 22.0 to 28.0%, Cu: 1.5 to 4.25%, Al: 0.12% or less, Ti: 0.05% or less, N: 0.008 to 0.140%, O (oxygen): 0.02% or less, at least one kind of a component selected from at least one group of the first group to the fifth group described below, the balance being Fe and impurities:
first group: Co: 10% or less,
second group: Mo: 5% or less, W: 5% or less, and Ta: 5% or less,
third group: B: 0.1% or less, V: 0.5% or less, Zr: 0.5% or less, Nb: 2% or less, and Hf: 0.5% or less,
fourth group: Mg: 0.1% or less and Ca: 0.1% or less,
fifth group: Y: 0.15% or less, La: 0.15% or less, Ce: 0.15% or less, and Nd: 0.15% or less.
8. The metal material according to claim 7 ,
characterized by having a fine grain size such that the austenite grain size is No. 6 or higher.