Preparation method and application of magnetic iron oxide and desulfurizer containing the magnetic iron oxide as active component
A method of preparing magnetic iron oxide Fe 21.333 O 32 , which includes the steps of preparing a solid green rust and calcining the solid green rust to obtain the magnetic iron oxide Fe 21.333 O 32 . Also provided is the application of magnetic iron oxide Fe 21.333 O 32 as an active material in desulfurization at a medium temperature. Also provided is a desulfurizer which uses magnetic iron oxide Fe 21.333 O 32 and the application thereof. The present preparation method has simple steps and a short production period.
1. A method of preparing magnetic iron oxide Fe 21.333 O 32 , which comprises preparing a solid green rust, and then calcining the solid green rust to obtain the magnetic iron oxide Fe 21.333 O 32 .
2. The method of claim 1 , wherein, the solid green rust is obtained by mixing and reacting a solid ferrous salt with a solid alkaline substance, or mixing and reacting a solution of ferrous salt with a solid alkaline substance, or mixing and reacting a solution of ferrous salt with a solution of an alkaline substance.
3. The method of claim 2 , wherein, said alkaline substance is a hydroxide or a carbonate.
4. The method of claim 3 , wherein, the molar ratio of the ferrous salt to the hydroxide is (1:2.08) ˜(1:2.22).
5. The method of claim 3 , wherein, the molar ratio of the ferrous salt to said carbonate is (1:1.04) ˜(1:1.1).
6. The method of claim 1 , wherein, the calcining is carried out at a temperature of 250° C. ˜400° C.
7. The method of claim 1 , wherein, the calcining is carried out at a temperature of 300° C˜350° C.
8. The method of claim 1 , wherein, the calcining lasts for 1-3 hours.
9. The method of claim 1 , wherein the calcining lasts for 1.5-2 hours.
10. The application of magnetic iron oxide Fe 21.333 O 32 obtained according to the method of claim 1 as an active material of desulfurization at a medium temperature of 250° C. to 400° C.
11. A desulfurizer, comprising magnetic iron oxide Fe 21.333 O 32 and a binder, wherein said magnetic iron oxide Fe 21.333 O 32 is prepared according to the preparation method of claim 1 .
12. The desulfurizer of claim 11 , wherein, said magnetic iron oxide Fe 21.333 O 32 constitutes 87-92 weight % of the desulfurizer, and said binder constitutes 8-13 weight % of the desulfurizer.
13. The desulfurizer of claim 11 , wherein, said binder is an organic binder.
14. The desulfurizer of claim 13 , wherein, further comprising a dispersing agent.
15. The desulfurizer of claim 14 , wherein, said magnetic iron oxide Fe 21.333 O 32 constitutes 87-92 weight % of the desulfurizer, and said binder constitutes 3-5 weight % of the desulfurizer, and said dispersing agent constitutes 4-8 weight % of the desulfurizer.
16. The desulfurizer of claim 14 , wherein, said dispersing agent is selected from the group consisting of active carbon powder, apricot stone carbon, coconut shell carbon, willow carbon powder, wooden carbon and coaly carbon and any combination thereof.
17. The desulfurizer of claim 11 , wherein, said binder is an inorganic binder.
18. The desulfurizer of claim 12 , wherein, said binder is an inorganic binder.
19. The desulfurizer of claim 17 , wherein, said inorganic binder is selected from the group consisting of bentonite, kaolin clay, attapulgite and Yang Gan soil and any combination thereof.