Sustainable injection molded articles
A sustainable thermoplastic composition made by forming a mixture of virgin polypropylene and post-industrial-recycled material (PIR). The PIR may include a thermoplastic, elastomeric-polymer and a spunbond component. The mixture is melt-blended in an extruder. Extruded materials made from the mixture demonstrate little variance in the results of the IZOD Impact Test of materials containing 30 to 70 percent PIR, and a material containing 100 percent virgin polypropylene. In addition, the extruded materials containing 30 to 70 percent PIR demonstrate a substantially constant strain at yield, that strain at yield being substantially equal to that demonstrated by a material containing 100 percent virgin polypropylene.
1. A thermoplastic material comprising:
30 to 70 parts by weight of 100% virgin polymer selected from the group consisting of polypropylene, polyethylene, polystyrene, acrylonitrile-butadiene-styrene copolymers, polylactic acid, blends of polylactic acid and polyolefins and combinations thereof; and
the remaining parts by weight of a post-industrial-recycled material (PIR), wherein the PIR comprises a spun-bonded laminate comprising a thermoplastic polyolefin elastomer and a spunbonded fiber layer or an adhesive spun-bond film laminate comprising a polyolefin film layer and a spunbonded fiber layer.
2. The material of claim 1 wherein the PIR comprises a styrenic, thermoplastic, block-copolymer.
3. The material of claim 1 having a 2 ft-lb hammer capacity impact-strength between 10 and 11 ft-lb f /in, according to an Izod Impact Strength Test Method described herein.
4. The material of claim 1 wherein the 100% virgin polymer has a 2 ft-lb hammer capacity impact-strength between 10 and 11 ft-lb f /in, according to an Izod Impact Strength Test Method described herein.
5. The material of claim 1 having a constant strain at yield.
6. The material of claim 1 wherein the virgin polymer is polypropylene.
7. A thermoplastic extruded article comprising:
a core layer of material, the core layer comprising 30 to 70 parts by weight of 100% virgin polymer selected from the group consisting of polypropylene, polyethylene, polystyrene, acrylonitrile-butadiene-styrene copolymers, polylactic acid, blends of polylactic acid and polyolefins and combinations thereof; and
the remaining parts by weight of a post-industrial-recycled material (PIR), wherein the PIR comprises a spun-bonded laminate comprising a thermoplastic polyolefin elastomer and a spunbonded fiber layer or an adhesive spun-bond film laminate comprising a polyolefin film layer and a spunbonded fiber layer.
8. The article of claim 7 , wherein the article is a package for wet wipes.
9. The article of claim 7 , further comprising two skin layers comprised of at least one virgin polymer, wherein the core layer is sandwiched between the two skin layers, and wherein the core layer and the skin layers together define an article thickness.
10. The article of claim 9 , wherein the layer of material comprises 51% to 90% of the article thickness, and the two skin layers each comprise 5% to 24.5% of the article thickness.
11. The article of claim 7 , wherein the core layer is formed by melt processing the virgin polymer and PIR at temperatures ranging from 160° C. to 240° C.
12. A thermoplastic material comprising:
30 to 70 parts by weight of 100% virgin polymer selected from the group consisting of polypropylene, polyethylene, polystyrene, acrylonitrile-butadiene-styrene copolymers, polylactic acid, blends of polylactic acid and polyolefins and combinations thereof; and
the remaining parts by weight of a post-industrial-recycled material (PIR), wherein the PIR comprises a spun-bonded laminate comprising a thermoplastic polyolefin elastomer and a gatherable fiber layer or an adhesive spun-bond film laminate comprising a polyolefin film layer and a nonwoven facing.
13. The material of claim 12 , wherein the PIR comprises a styrenic, thermoplastic, block-copolymer.
14. The material of claim 12 having a 2 ft-lb hammer capacity impact-strength between 10 and 11 ft-lb f /in, according to an Izod Impact Strength Test Method described herein.
15. The material of claim 12 , wherein the 100% virgin polymer has a 2 ft-lb hammer capacity impact-strength between 10 and 11 ft-lb f /in, according to an Izod Impact Strength Test Method described herein.
16. The material of claim 12 having a constant strain at yield.
17. The material of claim 12 , wherein the virgin polymer is polypropylene.