Method for making gas turbine engine composite structure
A method for making a gas turbine engine matrix composite structure. The method includes providing at least one metal core element, fabricating a matrix composite component about the metal core element, and removing at least part of the metal core element from the matrix composite component by introduction of a halogen gas.
1. A method for making a gas turbine engine matrix composite structure comprising:
providing at least one metal core element;
fabricating a matrix composite component about the metal core element; and
removing at least part of the metal core element from the matrix composite component by introduction of a halogen gas.
2. The method of claim 1 in which the matrix composite is composed of at least one selected from the group consisting of a SiC/SiC composite manufactured by a chemical vapor infiltration (CVI), slurry, and melt infiltration process, a SiC/SiC composite manufactured by a tow coating, tape casting, and lamination process, a SiC/SiC composite manufactured by a CVI, pre-ceramic polymer infiltration and pyrolysis process, an oxide/oxide composite manufactured by a tape casting, lamination, and sintering process, a C/C/SiC composite manufactured by a polymer carbonization, and melt infiltration process, and a C/SiC composite manufactured by a CVI process or a CVI, slurry, and melt infiltration process.
3. The method of claim 1 in which the metal core element is composed of at least one selected from the group consisting of:
yttrium, lanthanum, terbium, and ytterbium alloys containing less than 10% silicon;
zirconium and hafnium alloys including one or more of carbon, boron, nitrogen, oxygen, silicon, hafnium, tantalum, aluminum, and less than 10 atomic % of scandium, yttrium, titanium, vanadium, niobium, chromium, molybdenum, tungsten, cobalt, rhodium, iridium, nickel, germanium, tin, terbium, ytterbium;
boron alloys including one or more of Sn, Zn, Cu, titanium and titanium alloys including one or more of Si, B, Ge, Sn, germanium alloys including one or more of Si, B, Ti, Mo, Ni, Nb, Zr, Y, V, Co, and aluminum alloys including one or more of B, Si, Ti, Mo, Ni, Nb, Zr, Y, V, Co;
pure nickel, 51 Ge-49 Si alloy, and Ni—Si—Ge alloy.
4. The method of claim 1 in which the metal core element is fabricated by at least one of casting, forging, bending of sheet, bending of wire, machining, grinding, electrical discharge machining (EDM), laser cutting, water jet cutting, electroforming, welding of multiple pieces, brazing of multiple pieces, laser sintering, and powdered metal processing.
5. The method of claim 1 further comprising casting into the metal core element a material selected from the group consisting of: monolithic ceramic, ceramic matrix composite (CMC), and carbon.
6. The method of claim 1 in which the metal core element includes a plurality of pieces and at least two pieces have a different melting point.
7. The method of claim 1 further comprising bonding to the metal core element an element made of a material that is selected from the group consisting of monolithic ceramic, ceramic matrix composite (CMC), and carbon.
8. A method for making a gas turbine engine matrix composite turbine blade, comprising:
forming a metallic alloy core;
wrapping a plurality of ceramic fabric plies about the metallic alloy core to have substantially a turbine blade shape and to define an opening in the plurality of ceramic fabric plies that exposes at least a portion of the metallic alloy core to the outside of the plurality of ceramic fabric plies; and
heating the metallic alloy core and introducing a halogen gas to the metallic alloy core to remove at least a portion of the metallic alloy core through the opening in the plurality of ceramic fabric plies.
9. The method of claim 8 in which wrapping comprises extending one or more of the plurality of ceramic fabric plies beyond the metallic alloy core in a span direction of the turbine blade on both sides of the turbine blade.
10. The method of claim 8 in which the wrapping comprises shaping an upper portion of the plurality of ceramic fabric plies as a solid portion of the turbine blade.
11. The method of claim 8 in which the wrapping comprises integrating a lower portion of the plurality of the ceramic fabric plies with additional ceramic fabric plies to form a turbine blade platform.
12. The method of claim 11 in which forming the metallic alloy core comprises forming an extension in the lower portion of the plurality of the ceramic fabric plies that extends through the turbine blade platform of the turbine blade.
13. The method of claim 8 in which the halogen gas comprises chlorine gas.
14. The method of claim 8 in which the metallic alloy core comprises a metallic alloy foam.
15. The method of claim 8 in which the metallic alloy core comprises an alloy that is also used in the fabrication of the plurality of ceramic fabric plies.
16. The method of claim 8 further comprising coating the metallic alloy core with at least one of Si, Si, SiC, C, SiNC, Si 3 N 4 , B, Ir, Mo, Rh, Pd, Pt, Nb or ceramic oxides, nitrides, or borides.
17. The method of claim 16 in which the coating is applied by chemical vapor deposition (CVD), physical vapor deposition (PVD), plasma spray, brush or spray on slurry.
18. A method for making a gas turbine engine composite component, the method comprising:
forming a metal casting during which a carbon release film thereon is converted to SiC;
applying a layer of carbon to the metal casting;
wrapping the metal casting in a plurality of fabric layers to have substantially a gas turbine engine component shape;
infiltrating the wrapped metal casting with SiC chemical vapor infiltration; and
heating the wrapped metal casting and introducing a halogen gas to the metal casting to remove at least a portion of the metal casting.
19. The method of claim 18 in which forming the metallic alloy core comprises using chopped fiber with binder in branched areas of the metallic alloy core.