View Patent ↗Provided is a treatment method for fluororesin pellets to remove hydrofluoric acid released from fluororesin pellets obtained by melt-molding a melt-moldable fluororesin. The treatment method comprises bringing a hydrofluoric acid-removing medium selected from warm water of from 30 to 200° C., steam of from 100 to 200° C. and warm wind of from 40 to 200° C. into contact with fluororesin pellets obtained by melt-molding a melt-moldable fluororesin, and thereby treating the fluororesin pellets so that the amount of hydrofluoric acid released per kg of the resulting fluororesin pellets would be at most 5 μg as determined after the storage of the resulting fluororesin pellets at 35° C. for 15 days.
1. A treatment method for fluororesin pellets, which comprises contacting fluororesin pellets obtained by melt-molding a melt-moldable fluororesin with warm water at a temperature of from 30 to 200° C. for 10 seconds to 60 minutes, steam at a temperature of from 100 to 200° C. for 10 seconds to 60 minutes, or warm wind at a temperature of from 40 to 200° C. for 30 minutes to 2 hours so that the amount of hydrofluoric acid released per kg of the resulting fluororesin pellets would be at most 5 μg as determined after the storage of the resulting fluororesin pellets at 35° C. for 15 days.
2. The treatment method for fluororesin pellets according to claim 1 , wherein warm water at a temperature of from 30 to 200° C. is contacted with the fluororesin pellets for at 10 seconds to 1 minute.
3. The treatment method for fluororesin pellets according to claim 1 , wherein steam at a temperature of from 100 to 200° C. is contacted with the fluororesin pellets for 10 seconds to 1 minute.
4. The treatment method for fluororesin pellets according to claim 1 , wherein warm wind at a temperature of from 40 to 200° C. is contacted with the fluororesin pellets for 30 minutes to 1 hour.
5. The treatment method for fluororesin pellets according to claim 4 , wherein the volume flow rate of the warm wind is from 5 to 50 m 3 /hr.
6. The treatment method for fluororesin pellets according to claim 1 , wherein the average particle size of the fluororesin pellets is from 1.0 to 5.0 mm.
7. The treatment method for fluororesin pellets according to claim 6 , wherein the bulk density of the fluororesin pellets is from 0.5 to 1.5 g/ml.
8. The treatment method for fluororesin pellets according to claim 1 , wherein the bulk density of the fluororesin pellets is from 0.5 to 1.5 g/ml.
9. The treatment method for fluororesin pellets according to claim 1 , wherein the melt-moldable fluororesin is an ethylene/tetrafluoroethylene copolymer.
10. The treatment method for fluororesin pellets according to claim 9 , wherein the ethylene/tetrafluoroethylene copolymer comprises repeating units derived from tetrafluoroethylene, repeating units derived from ethylene and repeating units derived from a compound represented by CH 2 ═CX(CF 2 ) n Y wherein each of X and Y which are independent of each other, is a hydrogen atom or a fluorine atom, and n is an integer of from 2 to 8; the molar ratio of repeating units derived from ethylene/repeating units derived from tetrafluoroethylene is from 80/20 to 20/80; and the content of repeating units derived from the compound represented by CH 2 ═CX(CF 2 ) n Y is from 0.01 to 20 mol % to all repeating units in the ethylene/tetrafluoroethylene copolymer.
11. A treatment method for fluororesin pellets, which comprises contacting fluororesin pellets obtained by granulating fluororesin fine particles obtained by polymerization to produce fluororesin beads and melt-molding the fluororesin beads into pellet form with warm water at a temperature of from 30 to 200° C. for 10 seconds to 60 minutes, steam at a temperature of from 100 to 200° C. for 10 seconds to 60 minutes, or warm wind at a temperature of from 40 to 200° C. for 30 minutes to 2 hours so that the amount of hydrofluoric acid released per kg of the resulting fluororesin pellets would be at most 5 μg as determined after the storage of the resulting fluororesin pellets at 35° C. for 15 days.