Method of making a cathode slurry and a cathode
View Patent ↗A cathode slurry comprising organic solvent, lithium iron phosphate, polymeric binder, and at least one conductive agent, and from about 30 wt. % to about 40 wt. % solids is prepared. The cathode slurry may be coated onto at least one side of a substrate to form a cathode coated substrate. The cathode coated substrate may be dried to form a cathode. An anode and cathode may be contained within a housing with electrolyte to form a lithium ion cell.
1. A method of making a cathode slurry comprising organic solvent, lithium iron phosphate, polymeric binder, and at least one conductive agent, the cathode slurry comprising from about 30 wt. % to about 40 wt. % solids, the method comprising:
providing a premix comprising the lithium iron phosphate and the organic solvent;
forming a polymer solution by admixing the polymeric binder and the organic solvent;
admixing from about 50 wt. % to about 75 wt. % of the premix to the polymer solution to form a first mix;
combining at least one conductive agent to the first mix to form a second mix; and
admixing from about 25 wt. % to about 50 wt. % of the premix to the second mix to form the cathode slurry.
2. The method of claim 1 , wherein the method further comprises filtering the premix prior to admixing the premix to the polymer solution such that the premix has an average particle size of less than about 150 microns.
3. The method of claim 1 , wherein combining of the at least one conductive agent to the first mix comprises admixing a first conductive agent, and admixing a second conductive agent after admixing the first conductive agent to the first mix.
4. The method of claim 1 , wherein the cathode slurry is substantially free of grit.
5. The method of claim 1 , wherein the cathode slurry comprises from about 30 wt. % to about 37 wt. % solids.
6. The method of claim 1 , wherein the solids comprise from about 75 wt. % to about 95 wt. % of lithium iron phosphate, from about 1 wt. % to about 10 wt. % of the polymeric binder, and from about 1 wt. % to about 10 wt. % of the at least one conductive agent.
7. The method of claim 1 , wherein the polymeric binder is selected from the group consisting of polyvinylidene difluoride (PVDF)-based polymers, polytetrafluoroethylene (PTFE), an acrylic copolymer, carboxymethyl cellulose, styrene-butadiene rubber (SBR), polybutadiene, polyvinyl alcohol, sodium polyacrylic acid, polyacrylonitrile, and combinations thereof.
8. The method of claim 1 , wherein the at least one conductive agent is selected from the group consisting of natural graphite, synthetic graphite, carbon black, acetylene black, partially graphitized coke, carbon nanotubes, fullerene, graphene, and combinations thereof.
9. The method of claim 1 , wherein admixing is performed by a mixer selected from the group consisting of shear mixers, planetary mixers, dispersers, rotary blade mixers, high intensity mixers, and combinations thereof.
10. A method of forming a cathode, the method comprising:
preparing a cathode slurry according of claim 1 , wherein the cathode slurry comprises from about 30 wt. % to about 37 wt. % solids;
depositing the cathode slurry onto at least one side of a substrate to form a cathode coated substrate; and
drying the cathode coated substrate to form the cathode.
11. The method of claim 10 , wherein depositing is performed by a coater selected from the group consisting of slot die coater, roll coater, reverse gravure, screen printer, and combinations thereof.
12. The method of claim 10 , wherein the cathode has an average thickness ranging from about 15 microns to about 150 microns.
13. The method of claim 12 , wherein the cathode has a thickness variance across the cathode surface of less than 10 wt. %.