Silicone-acrylic copolymer
View Patent ↗A novel silicone-acrylic copolymer which comprises a covalently bonded silicone polymer with an acrylic polymer through the —Si—O—Si— linkage is described. The silicone-acrylic copolymer is a reaction product of (a) a silicone polymer, (bi) a mixture of acrylic monomers wherein at least one acrylic monomer comprises a silane (meth)acrylic monomer and/or a siloxane (meth)acrylic macromer with a radical initiator to form an acrylic prepolymer or (bii) an acrylic polymer which comprises a silane or a siloxane functional group; and (c) a scrambling catalyst, wherein the ratio of the silicone polymer (a) and the mixture of acrylic monomers (bi) or polymer (bii) is from 50:1 to 1:50. The silicone-acrylic copolymer is useful as an adhesive, sealant, coating, and the like.
1. A silicone-acrylic copolymer comprising a silicone polymer and an acrylic polymer which are covalently bonded through —Si—O— linkage,
wherein the ratio of the silicone polymer and the acrylic polymer is from 50:1 to 1:50;
wherein the acrylic polymer is functionalized along the backbone with at least one silane or siloxane functional group that is an alkoxysilyl functional group selected from trimethoxylsilyl group, dimethoxymethylsilyl group, triethoxylsilyl group, diethoxymethylsilyl group or mixtures thereof;
wherein the acrylic polymer is prepared from acrylic monomers selected from butyl acrylate, 2-ethylhexyl acrylate, isooctyl acrylate, methyl acrylate, methyl methacrylate, t-octyl acrylamide, hydroxyethyl acrylate and acrylic acid, hydroxypropyl acrylate, hydroxylpropyl methacrylate, a nitrogen containing monomer or mixtures thereof
wherein the silicone-acrylic copolymer is a comb structure with a plurality of silicone polymer grafted onto the acrylic polymer backbone; and
wherein the silicone-acrylic copolymer forms a single phase in an organic solvent.
2. The silicone-acrylic copolymer of claim 1 wherein the silicone polymer is an organodisubstituted polysiloxane which is end-capped with a hydroxyl functional group, alkoxy functional group, hydride functional group, vinyl functional group or mixtures thereof.
3. The silicone-acrylic copolymer of claim 1 wherein the silicone polymer has an average molecular weight of from about 100 g/mol to 2,000,000 g/mol.
4. An article comprising the silicone-acrylic copolymer of claim 1 .
5. The article of claim 4 which is a coating, sealant or adhesive.
6. The article of claim 5 wherein the adhesive is a solution adhesive, emulsion adhesive or a hot melt adhesive.
7. The silicone-acrylic copolymer of claim 1 where the nitrogen containing monomer is selected from the group consisting of N-vinyl pyrrolidone, N-vinyl caprolactam, N-tertiary octyl acrylamide, dimethyl acrylamide, diacetone acrylamide, N-tertiary butyl acrylamide, N-isopropyl acrylamide, cyanoethylacrylate, N-vinyl acetamide, N-vinyl formamide and mixtures thereof.
8. A composition comprising (1) a silicone resin and (2) a silicone-acrylic copolymer and an acrylic polymer which are covalently bonded through a —Si —O— linkage;
wherein the silicone resin comprises at least one tetrafunctional siloxyl unit SiO 4/2 and at least one triorganosiloxy unit R 3 SiO 1/2 , wherein the R is methyl, hydroxyl, vinyl, phenyl, (meth)acryloxy or mixtures thereof, and the mole ratio of the units SiO 4/2 to R 3 SiO 1/2 is from 1:2 to 2:1;
wherein the ratio of the silicone polymer and the acrylic polymer is from 50:1 to 1:50;
wherein the acrylic polymer contains at least one silane or siloxane functional group;
wherein the silicone-acrylic copolymer is a comb structure with a plurality of silicone polymer grafted onto the acrylic polymer backbone; and
wherein the silicone-acrylic copolymer forms a single phase in an organic solvent.
9. The composition of claim 8 further comprising a tackifier, solubilizing agents, polyester, polyether, polyurethane, natural rubber, synthetic rubber, antioxidant, viscosity modifying agent, filler or mixtures thereof.
10. The composition of claim 8 wherein the amount of R groups is from about 0.05 wt % to 10 wt % based on the total weight of the silicone resin.