Free-formed quartz glass ingots and method for making same
View Patent ↗A method to form quartz glass ingots of ultra low contamination and defect levels by firing a high-purity quartz form as the feedstock, wherein the quartz glass ingot is free-formed on a platen rotating concentrically with the feedstock quartz article.
1. A process for manufacturing a quartz glass ingot, comprising the steps of:
providing a fabricated quartz glass article as a feedstock,
feeding the fused quartz glass feedstock into a furnace containing a platen rotating in axial symmetry to the quartz glass feedstock,
heating the fused quartz glass feedstock to a temperature sufficient for the quartz feedstock to melt, and
varying the temperature, the speed of the rotating platen, or both during the manufacturing process, thus forming the quartz glass ingot on the rotating platen in the absence of a container or mold.
2. The process of claim 1 , further comprising the step of annealing the fabricated quartz glass article prior to feeding the quartz glass article as feedstock to the furnace.
3. The process of claim 1 , further comprising the step of fusing a plurality of quartz rod segments into a fabricated quartz glass article prior to feeding the quartz glass article as feedstock to the furnace.
4. The process of claim 1 , wherein the axial symmetry has a maximum eccentricity of no more than one feedstock diameter between the axes of the feedstock and the ingot.
5. The process of claim 1 , wherein the quartz feedstock is selected from at least one of rods and tubings.
6. The process of claim 1 , wherein the quartz glass ingot is formed at a rate between about 5 and 50 pounds per hour.
7. The process of claim 1 , wherein the quartz glass ingot is formed at a rate between 10 and 20 pounds per hour.
8. The process of claim 1 , wherein a heat source is used to apply heat either indirectly or directly onto the quartz glass feedstock, and wherein the heat source is at least one selected from the group consisting of: resistive heating, RF heating, microwave heating, laser heating, electron beam heating, plasma torch heating, zone heating, induction heating, and burner.
9. The quartz glass article of claim 8 , wherein the heat source is at least one selected from the group consisting of: a single top center burner, multiple side burners, and multiple top-side burners.