Melt-fabricable perfluoropolymers having improved heat aging property
View Patent ↗Heat aging of the composition comprising melt-fabricable tetrafluoroethylene/perfluoro(alkyl vinyl ether) copolymer, the alkyl containing 1 to 5 carbon atoms and melt flowable polytetrafluoroethylene is effective to cause thermal transformation of the composition in the solid state, which is epitaxial co-crystallization of the polymer components of the composition, and other valuable changes, such as increased continuous use temperature.
1. Heat-aged composition comprising melt-fabricable tetrafluoroethylene/perfluoro(alkyl vinyl ether) copolymer, wherein said perfluoroalkyl contains 1 to 5 carbon atoms, and melt flowable polytetrafluoroethylene, the heat aging of said heat aged composition being carried out at a temperature greater than 260° C. with said composition being in the solid state, said heat aged composition exhibiting one or more of the following:
(a) a continuous use temperature of at least 300° C.,
(b) a reduced coefficient of friction,
(c) a reduced permeation to gases by at least 50%,
(d) a decrease in melt flow rate of at least 25% as compared to the melt flow rate of said composition prior to heat aging,
(e) an increase of at least 30% in storage modulus at 300° C.
(f) an increase in thickness of its crystalline layer characterized by an increase in long period of at least 25%,
(g) an increased resistance to sagging and/or ballooning,
(h) an increase in crystallinity index by at least 10%,
(i) improvement in uniformity of crystal structure characterized by an increase in long period coherence of at least 10%,
(j) an increase in thickness of crystalline layer characterized by an increase in long period of at least 25%,
(k) epitaxial co-crystallization.
2. The heat-aged composition of claim 1 in the form of electrical insulation, lining, heat exchanger elements, including tubes, self-supporting articles, including baskets and carriers, and tubing.
3. Heat-aged composition comprising melt-fabricable tetrafluoroethylene/perfluoro(alkyl vinyl ether) copolymer, wherein said perfluoroalkyl contains 1 to 5 carbon atoms, and an effective amount of melt flowable polytetrafluoroethylene to provide said heat aged composition with a crystal structure, characterized by one or more of the following: an increase in crystallinity index (i) of at least 10% as compared to said heat-aged composition prior to heat aging, and/or (ii) of at least 10% greater than the % increase in crystallinity index for said copolymer by itself upon said heat aging, wherein the heat aging of said heat aged composition is carried out at a temperature greater than 260° C. with said composition being in the solid state.
4. The heat aged composition of claim 3 exhibiting one or more of the following:
(i) uniformity of said crystal structure that is improved by said heat aging, characterized by said heat-aged composition exhibiting an increase in long period coherence that is at least 10% greater than the increase in long period coherence for said copolymer by itself upon said heat aging,
(ii) said crystal structure including lamellae comprising a crystalline layer of said heat-aged composition and an amorphous layer of said heat-aged composition, and the amount of said polytetrafluoroethylene is effective to increase the thickness of said crystalline layer, characterized by said heat-aged composition exhibiting an increase in long period of at least 25% upon said heat aging,
(iii) an apparent crystallite size of at least 280 angstroms, a crystallinity index of at least 44, a long period of at least 375 angstroms and a long period coherence of at least 450 angstroms, and
(iv) a 300° C. storage modulus that is at least 30% greater than the 300° C. storage modulus of said tetrafluoroethylene/perfluoro(alkyl vinyl ether) copolymer by itself after said heat aging is at 315° C. for 7 days.