Composite material comprising UHMWPE and iron ore tailing and use of iron ore tailing in preparation of composite material
The present invention relates to a composite material that comprises a polymeric constituent and iron ore powder. The polymeric constituent of the present invention is preferably UHMWPE. The iron ore powder used for the purposes of the present invention is the raw iron ore tailing resulting from iron ore pelletizing processes and it is used in an amount of 3-5% (w/w). The present invention is also related to the use of iron ore tailing in the preparation of composite materials comprising UHMWPE which presents improved properties such as creep resistance, stiffness and wear resistance, as well as cost reduction and reuses tailings of industrial plant. The present invention is also related to the use of the composite material of interest in the preparation of composite polymeric sheets for use in mining companies facilities.
1. A composite material for use in a mining process, comprising:
a polymeric sheet comprising:
ultra-high molecular weight polyethylene (“UHMWPE”); and
iron ore powder in an amount of 3-5% (w/w).
2. The composite material according to claim 1 , wherein the UHMWPE has an average molecular weight of above 7.0×10 6 g/mol.
3. The composite material according to claim 1 , wherein the iron ore powder is raw iron ore tailing resulting from iron ore pelletizing processes.
4. The composite material according to claim 3 , wherein the iron ore powder is in the amount of 3% (w/w).
5. A method of preparing a composite material for use in a mining process, comprising:
pelletizing iron ore including producing iron ore tailing as a byproduct of the pelletizing;
combining the iron ore tailing with ultra-high molecular weight polyethylene (“UHMWPE”), wherein the iron ore tailing is in an amount of 3-5% (w/w), and wherein the composite material has improved properties of creep resistance, stiffness and wear resistance as compared to UHMWPE alone; and
preparing the combined iron ore tailing and UHMWPE into a polymeric sheet.
6. A method of using the composite material according to claims 1 , 2 , 3 or 4 , comprising:
preparing a composite polymeric sheet and using the polymeric sheet in a mining facility.
7. The method of claim 6 , wherein using the sheets in a mining facility comprises using the sheets in at least one of coating silos, or channels of transfer conveyor belts, or scrapers, or screen rollers, or plows, or mixers, or pellet discs, or transfer points of ore and pellet.
8. The method of claim 6 , wherein preparing sheets comprises at least one of extruding or pressing the composite material to form the sheets.
9. The method of claim 5 , wherein the combining comprises mixing the iron ore tailing in the amount of 3% (w/w) with the UHMWPE having an average molecular weight of about 7.0×10 6 to 9.0×10 6 g/mol.
10. The method of claim 5 , wherein the iron ore tailing has a particle size distribution, based on sieving, which ranges from about 25 μm to about 90 μm.
11. The method of claim 5 , wherein the iron ore tailing has an average particle size, based on sieving, of about 38 μm.
12. The method of claim 11 , wherein the UHMWPE has an average particle size of about 132 μm.
13. The composite material according to claim 1 , wherein the iron ore tailing has a particle size distribution, based on sieving, which ranges from about 25 μm to about 90 μm.
14. The composite material according to claim 1 , wherein the iron ore tailing has an average particle size, based on sieving, of about 38 μm.
15. The composite material according to claim 14 , wherein the UHMWPE has an average particle size of about 132 μm.
16. The composite material according to claim 1 , wherein the polymeric sheet has a thickness of about 10 mm.
17. The composite material according to claim 1 , wherein the polymeric sheet is sized to support ore and pellets during mining processes.
18. The method of claim 5 , wherein the iron ore tailing is untreated before combining the iron ore tailing with the ultra-high molecular weight polyethylene.