Solvent-free method for making ethylene propylene diene polymer latex

1. A solvent free method for making a solvent free ethylene propylene diene terpolymer latex formulation, the method comprising:

a. blending water with 1 weight percent to 50 weight percent surfactant forming a solution;

b. blending solvent free ethylene propylene diene terpolymer with the solution at a pressure from 0.5 atm to 1.5 atm without an applied vacuum to form a terpolymer mixture, wherein solvent free ethylene propylene diene terpolymer is 10 weight percent to 60 weight percent of the total terpolymer weight of a final solvent free ethylene propylene diene terpolymer latex formation;

wherein the solvent free ethylene propylene diene terpolymer comprises:

(i) 85 weight percent to 99.75 weight percent of a random covalently linked polymer with saturated polymer backbones of ethylene and propylene, the ethylene and propylene having weight ratios from 40:60 to 85:15 of ethylene:propylene respectively, and a molecular weight from 100000 Mw to 5000 Mw; and

(ii) 0.25 weight percent to 15 weight percent of a non-conjugated diene component consisting of at least one of: a methylidene norbornene, a dicyclopentadiene, an ethylidene norbornene, a 1,4-hexadiene, norbornadiene, and a vinyl norbornene; and

c. high shear mixing the terpolymer mixture at from 0.5 atm to 1.5 atm for 5 minutes to 24 hours at a temperature from 20 degrees Celsius to 100 degrees Celsius to form a final solvent free ethylene propylene diene terpolymer latex formation, wherein the final solvent free ethylene propylene diene terpolymer latex formation has a viscosity from 1 centipoise to 2000 centipoise; a density from 0.8 to 1.1; and a shelf life of from 7 days to 365 days without separating or stratifying.

2. The solvent free method of claim 1 , wherein the surfactant is at least one of: cationic surfactant, anionic surfactant, and non-ionic surfactant.

3. The solvent free method of claim 2 , wherein the cationic surfactant, if used is at least one of: a dodecyl ammonium bromide and a tetra-octyl ammonium chloride, the anionic surfactant, if used is at least one of: sodium dodecyl benzene sulfonate and sulfo-succinate; and the non-ionic surfactant, if used is at least one of: a polyoxyethylene p-t-octylphenol and a polyoxyethylene sorbate.

4. The solvent free method of claim 1 , wherein the water for forming the solution is at least one of: distilled water, deionized water, tap water, and process water.

5. The solvent free method of claim 1 , further comprising adding 0.1 weight percent to 10 weight percent of a curative based on the total weight percent of the final solvent free ethylene propylene diene terpolymer latex formation to the final solvent free ethylene propylene diene terpolymer latex formulation forming a curable solvent free ethylene propylene diene terpolymer latex.

6. The solvent free method of claim 5 , further comprising applying a heating to the curable solvent free ethylene propylene diene terpolymer latex at a temperature ranging from 25 degrees Celsius to 100 degrees Celsius ranging from 10 minutes to 24 hours, at a pressure from 0.5 atm to 1.5 atm without an applied vacuum forming a partially cross-linked solvent free ethylene propylene diene terpolymer latex formulation.

7. The solvent free method of claim 6 , wherein in the heating achieves from 20 percent to 98 percent cross-linking in the partially cross-linked solvent free ethylene propylene diene terpolymer latex formulation.

8. The solvent free method of claim 5 , adding 0.1 weight percent to 10 weight percent of a sulfur accelerator into the curative based on the total weight percent of the curative.

9. The solvent free method of claim 1 , further comprising adding 0.1 weight percent to 3 weight percent of a defoaming agent to the solution based on the total weight percent of the final solvent free ethylene propylene diene terpolymer latex formation or adding the defoaming agent to the terpolymer mixture.

10. The solvent free method of claim 9 , wherein the defoaming agent is at least one of: a silicone glycol, a polyethylene glycol, a polyacrylate, a poly-dimethyl siloxane, and a poly-dimethyl siloxane with finely divided silica.

11. The solvent free method of claim 1 , further comprising adding 1 weight percent to 5 weight percent of an anti-settling stabilizer to the final solvent free ethylene propylene diene terpolymer latex formation based on the weight percent of the final solvent free ethylene propylene diene terpolymer latex formation.

12. The solvent free method of claim 1 , further comprising adding 0.1 weight percent to 3 weight percent of a biocide to the final solvent free ethylene propylene diene terpolymer latex formation based on the total weight percent of the final solvent free ethylene propylene diene terpolymer latex formation.

13. The solvent free method of claim 1 , further comprising adding 5 weight percent to 50 weight percent of a filler to the final solvent free ethylene propylene diene terpolymer latex formation based on the total weight percent of the final solvent free ethylene propylene diene terpolymer latex formation.

14. The solvent free method of claim 1 , further comprising adding 0.1 weight percent to 20 weight percent of a pigment to the final solvent free ethylene propylene diene terpolymer latex formation based on the total weight percent of the final solvent free ethylene propylene diene terpolymer latex formation.

15. The solvent free method of claim 6 , wherein the heating can be performed using a heat exchanger, a heat transfer fluid, electrical heat, steam, or combinations thereof.

16. The solvent free method of claim 5 , wherein the curative is selected from the group consisting of: sulfur, derivatives of sulfur, peroxide, hydroperoxide, peroxy-carbonate, thiuram, thiazole, dithiocarbamate, and xanthate.

17. The solvent free method of claim 8 , wherein the sulfur accelerator is selected from the group consisting of: zinc diethyldithiocarbamate and zinc benzothiozole.

18. The solvent free method of claim 11 , wherein the anti-settling stabilizer is glycerin.

19. The solvent free method of claim 12 , wherein the biocide is benzisothiazolinone.

20. The solvent free method of claim 13 , wherein the filler is selected from the group consisting of: a silica, a talc, a starch, a calcium carbonate, and a carbon black.

21. The solvent free method of claim 14 , wherein the pigment is selected from the group consisting of: an organic dye, a carbon black, and a metal oxide.