Composite including conductive material and binder on surface of (semi) metal oxide and method of preparing anode slurry including the same

1. An anode slurry comprising:

a) a composite comprising:

a (semi) metal oxide;

an aqueous binder disposed on a surface of the (semi) metal oxide; and

a conductive material dispersed in the aqueous binder,

b) a non-aqueous binder;

c) a conductive agent; and

d) a carbon material.

2. The anode slurry of claim 1 , wherein the (semi) metal oxide comprises one or more selected from the group consisting of SiO x , AlO x , SnO x , SbO x , BiO x , AsO x , GeO x , PbO x , ZnO x , CdO, x , InO x , TiO x , and GaO x , where 0<x<2.

3. The anode slurry of claim 1 , wherein the aqueous binder comprises one or more selected from the group consisting of a styrene-butadiene rubber, an acrylonitrile-butadiene rubber, an acrylonitrile-butadiene- styrene rubber, carboxymethyl cellulose, and hydroxypropyl methylcellulose.

4. The anode slurry of claim 1 , wherein the non-aqueous binder includes one or more selected from the group consisting of polytetrafluoroethylene (PTFE), polyvinylidene fluoride (PVdF), polyvinylpyrrolidone, tetrafluoroethylene, polyethylene, and polypropylene.

5. The anode slurry of claim 1 , wherein the carbon material includes one or more selected from the group consisting of soft carbon, hard carbon, natural graphite, artificial graphite, Kish graphite, pyrolytic carbon, mesophase pitch-based carbon fibers, mesocarbon microbeads, mesophase pitch, petroleum-derived cokes, and coal-derived cokes.

6. The anode slurry of claim 1 , wherein the conductive material comprises one or more selected from the group consisting of carbon black selected from the group consisting of carbon black, acetylene black, Ketjen black, channel black, furnace black, lamp black, and thermal black; conductive fibers selected from the group consisting of carbon fibers and metal fibers; metal powder selected from the group consisting of fluorocarbon powder, aluminum powder, and nickel powder; conductive whiskers selected from the group consisting of zinc oxide and potassium titanate; conductive metal oxide including titanium oxide; and a polyphenylene derivative.

7. The anode slurry of claim 1 , wherein the conductive material is uniformly dispersed in the aqueous binder.

8. The anode slurry of claim 1 , wherein the conductive material is coupled to the surface of the (semi) metal oxide by the aqueous binder.

9. A secondary battery comprising:

a cathode including a cathode active material;

a separator;

an anode including the anode slurry of claim 1 ; and

an electrolyte.

10. A method of preparing an anode slurry, the method comprising:

preparing a composite by dispersing a conductive material in an aqueous binder and then mixing the aqueous binder in which the conductive material is dispersed with a (semi) metal oxide, wherein the aqueous binder is disposed on a surface of the (semi) metal oxide; and

mixing the composite with a carbon material, a conductive agent, and a non-aqueous binder.

11. The method of claim 10 , wherein the conductive material is included in an amount ranging from 1 part by weight to 20 parts by weight based on a total weight of the aqueous binder.

12. The method of claim 10 , wherein the preparing of the composite is performed by a spray drying method.

13. The method of claim 10 , wherein the carbon material comprises one or more selected from the group consisting of soft carbon, hard carbon, natural graphite, artificial graphite, Kish graphite, pyrolytic carbon, mesophase pitch-based carbon fibers, mesocarbon microbeads, mesophase pitch, petroleum-derived cokes, and coal-derived cokes.

14. The method of claim 10 , wherein the carbon material is included in an amount ranging from 20 parts by weight to 80 parts by weight based on a total weight of the composite.

15. The method of claim 10 , wherein the non-aqueous binder comprises one or more selected from the group consisting of polytetrafluoroethylene (PTFE), polyvinylidene fluoride (PVdF), polyvinylpyrrolidone, tetrafluoroethylene, polyethylene, and polypropylene.