Composite for anode active material and method of preparing the same
View Patent ↗Provided are a composite for an anode active material and a method of preparing the same. More particularly, the present invention provides a composite for an anode active material including a (semi) metal oxide and an amorphous carbon layer on a surface of the (semi) metal oxide, wherein the amorphous carbon layer comprises a conductive agent, and a method of preparing the composite.
1. An anode slurry comprising:
i) a composite for an anode active material comprising a core consisting of a core oxide selected from the group consisting of metal oxide, semi metal oxide and a mixture thereof;
an amorphous carbon layer coated on a surface of the core oxide; and
a conductive agent for the composite dispersed in the amorphous carbon layer,
wherein the amorphous carbon layer forms a matrix and the conductive agent is dispersed as a filler in the matrix;
ii) a conductive agent for the anode slurry;
iii) a binder; and
iv) a natural graphite.
2. The anode slurry of claim 1 , wherein the core oxide comprises one or more selected from the group consisting of SiO x , AlO x , SnO x , SbO x , BiO x , AsO x , GeO x , PbO x , ZnO x , CdO, x InO x , TiO x , and GaO x ,
where 0<x<2.
3. The anode slurry of claim 1 , wherein the conductive agent for the composite is one or more selected from the group consisting of carbon nanotubes, carbon nanofibers, graphene, carbon black, acetylene black, Ketjen black, channel black, furnace black, lamp black, and thermal black.
4. The anode slurry of claim 1 , wherein the conductive agent for the composite is selected from the group consisting of crystalline carbon, amorphous carbon, and a mixture thereof.
5. The anode slurry of claim 1 , wherein an amount of the conductive agent for the composite is in a range of 1 wt % to 20 wt % based on a total weight of the core oxide.
6. The anode slurry of claim 1 , wherein a carbon content of the amorphous carbon layer is 2 parts by weight to 30 parts by weight based on 100 parts by weight of the core oxide.
7. The anode slurry of claim 1 , wherein the entire or partial surface of the core oxide is coated with the amorphous carbon layer.
8. The anode slurry of claim 1 , wherein a thickness of the amorphous carbon layer is in a range of 5 nm to 70 nm.
9. A secondary battery comprising:
a cathode including a cathode active material;
a separator;
an anode prepared from the anode slurry of claim 1 ; and
an electrolyte.