Method for preparing anode active material, anode active material prepared therefrom and lithium secondary battery having the same
View Patent ↗The present invention relates to a method for preparing an anode active material, comprising (S1) forming a shell being a coating layer comprising a carbon material on the surface of a core comprising silicon oxide particles, to obtain a silicon oxide-carbon composite having a core-shell structure; (S2) mixing the silicon oxide-carbon composite with an oxygen-containing lithium salt, followed by heat treatment to produce a silicon oxide-lithium alloy, thereby obtaining a (SiO x —Li y )—C (0<x<1.5, 0<y<4) composite having a core-shell structure; and (S3) washing the surface of the (SiO x —Li y )—C composite having a core-shell structure and drying the composite, and an anode active material prepared by the method.
1. A lithium secondary battery, comprising:
a cathode;
an anode; and
a separator interposed between the cathode and the anode, wherein the anode comprises:
a current collector; and
an anode active material layer formed on at least one surface of the current collector and comprising an anode active material, wherein the anode active material comprising a core-shell structured (SiO x —Li y )—C composite (0<x<1.5, 0<y<4) which has a core comprising (SiO x —Li y ), and a shell coated on the surface of the core and comprising a carbon material,
wherein the core-shell structured (SiO x —Li y )—C composite comprises an unreacted oxygen-containing lithium salt in an amount of 5 wt % or less, and by-products of the reaction between an oxygen-containing lithium salt and silicon oxide in an amount of 10 wt % or less, and
wherein the battery has a normalized capacity at the 50 th cycle of greater than 85%.
2. The lithium secondary battery according to claim 1 , wherein the carbon material is crystalline carbon or amorphous carbon.
3. The lithium secondary battery according to claim 1 , wherein the core comprising silicon oxide particles has a diameter of 0.05 to 30 μm.
4. The lithium secondary battery according to claim 1 , wherein in the shell being a coating layer comprising a carbon material, the carbon material is present in an amount of 0.05 to 30 wt % based on the weight of the anode active material.
5. The lithium secondary battery according to claim 1 , wherein the by-products of the oxygen-containing lithium salt is LiOH, Li 2 CO 3 , Li 4 SiO 4 , Li 2 Si 3 O 5 , Li 2 Si 2 O 5 , Li 8 O 2 (SiO 4 ), Li 6 (Si 2 O 7 ), or a mixture thereof.