Separator and electrochemical device having the same

1. A method of preparing a separator, comprising:

providing a planar and porous substrate having multiple pores;

providing a slot-die comprising a slot section and a slide section; and

coating a first slurry on at least one surface of the porous substrate through the slot section to form a porous coating layer, while continuously coating a second slurry on the porous coating layer through the slide section adjacent to the slot section only by the force of gravity to form a layer for adhesion with an electrode,

wherein the first slurry for forming the porous coating layer comprises inorganic particles, a first binder polymer and a first solvent,

wherein the second slurry for forming the layer for adhesion comprises a second binder polymer and a second solvent,

wherein the first binder polymer and the second binder polymer are each independently selected from polyvinylidene fluoride-co-hexafluoro propylene, polyvinylidene fluoride-co-trichloro ethylene, polyvinylidene fluoride-co-chlorotrifluoro ethylene, polymethyl methacrylate, polyacrylonitrile, polyvinylpyrrolidone, polyvinylacetate, polyethylene-co-vinyl acetate, polyethylene oxide, cellulose acetate, cellulose acetate butyrate, cellulose acetate propionate, cyanoethyl pullulan, cyanoethyl polyvinylalcohol, cyanoethyl cellulose, cyanoethyl sucrose, pullulan, carboxyl methyl cellulose, acrylonitrile-styrene-butadiene copolymer, polyimide or a mixture thereof,

wherein the first slurry and the second slurry each independently have a viscosity of 10 to 20 cp,

wherein the first slurry is discharged at a rate faster than that of the second slurry,

wherein the layer for adhesion has a thickness of 0.0005 μm to 1 μm, and

wherein the slide section is inclined to form an angle (θ) of 10 to 60° with the slot section.

2. The method of claim 1 , wherein the first slurry is discharged at a rate of 500 to 2,000 ml/min, and the second slurry is discharged at a rate of 200 to 1,200 ml/min.

3. The method of claim 1 , wherein the layer for adhesion with an electrode has a thickness satisfying 1/10 or less of the thickness of the porous coating layer.

4. The method of claim 1 , wherein the porous substrate is a polyolefin-based porous membrane.

5. The method of claim 1 , wherein the slot section and the slide section are formed in an integrated slide-slot die, or independently formed in a slot die and a slide die, respectively.

6. The method of claim 1 , wherein the inorganic particles have an average diameter of 0.001 to 10 μm.

7. The method of claim 1 , wherein the inorganic particles are selected from inorganic particles having a dielectric constant of 5 or higher, inorganic particles having the ability to transport lithium ions, or a mixture thereof.

8. The method of claim 7 , wherein the inorganic particles having a dielectric constant of 5 or higher are selected from the group consisting of BaTiO 3 , Pb(Zr x ,Ti 1-x )O 3 (PZT, 0<x<1), Pb 1-x La x Zr 1-y Ti O 3 (PLZT, 0<x<1, 0<y<1), (1-x) Pb(Mg 1/3 Nb 2/3 )O 3-x PbTiO 3 (PMN-PT, 0<x<1), hafnia (HfO 2 ), SrTiO 3 , SnO 2 , CeO 2 , MgO, NiO, CaO, ZnO, ZrO 2 , Y 2 O 3 , Al 2 O 3 , SiC, TiO 2 inorganic particles or a mixture thereof.

9. The method of claim 7 , wherein the inorganic particles having the ability to transport lithium ions are selected from lithium phosphate (Li 3 PO 4 ), lithium titanium phosphate (Li x Ti y (PO 4 ) 3 , 0<x<2, 0<y<3), lithium aluminum titanium phosphate (Li x Al y Ti z (PO 4 ) 3 , 0<x<2, 0<y<1, 0<z<3), (LiAlTiP) x O y type glass (0<x<4, 0<y<13), lithium lanthanum titanate (Li x La y TiO 3 , 0<x<2, 0<y<3), lithium germanium thiophosphate (Li x Ge y P z S w , 0<x<4, 0<y<1, 0<z<1, 0<w<5), lithium nitride (Li x N y , 0<x<4, 0<y<2), SiS 2 type glass (Li x Si y S z , 0<x<3, 0<y<2, 0<z<4), P 2 S 5 type glass (Li x P y S z , 0<x<3, 0<y<3, 0<z<7) inorganic particles, or a mixture thereof.

10. A separator prepared by the method of claim 1 .

11. An electrochemical device, comprising a cathode, an anode and a separator interposed between the cathode and the anode,

wherein the separator is defined in claim 10 .

12. The electrochemical device according to claim 11 , which is a lithium secondary battery.