Sugar-based polyurethanes, methods for their preparation, and methods of use thereof
Polyurethane foams which are highly flame resistant are described, as well as the production of such polyurethane foams by the reaction between a natural polyol, such as sucrose or a blend of mono- or disaccharides in place of the standard hydrocarbon-based polyol component, a polyisocyanate and water in the presence of a suitable polyurethane forming catalyst and a non-halogenated flame retardant, and optionally one or more components such as surfactants and/or emulsifiers. The resultant polyurethane foam has a bio-based solid content ranging from about 17% to 30%, may be formulated in a variety of foam densities for a variety of applications, and exhibits a high degree of fire and burn resistance, as exhibited by the flame spread index, flash over resistance determination, and the smoke spread values.
1. A flame-retardant polyurethane foam comprising the reaction product of:
a first reaction mixture consisting of at least one polyisocyanate and optionally a surfactant; and
a second reaction mixture consisting of:
a natural polyol wherein substantially all of the hydroxyl groups on the polyol are free;
a non-halogenated inorganic hydrate or inorganic hydroxide flame retardant;
a surfactant;
an aqueous blowing agent;
a polyurethane producing catalyst; and
optionally, any one or any combination of a plasticizer, an emulsifier, a biocide, a bacteriostat, a polyether polyol, a halogenated or non-halogen containing blowing agent, a filler, a dye or colorant, an anti-scorching agent, glycerine, a chain extender/cross-linker, an antioxidant, an antistatic agent, and/or a cell-opening agent;
wherein the first reaction mixture and the second reaction mixture are used in amounts to provide an Isocyanate Index of 20 to 50.
2. The polyurethane foam according to claim 1 , wherein the natural polyol is selected from the group consisting of sucrose, fructose, glucose, xylose, corn syrup, dextrose, and molasses.
3. The polyurethane foam according to claim 1 , wherein the non-halogenated flame retardant is an aluminum, barium, calcium, copper, iron, magnesium, nickel, or zinc hydroxide or hydrate.
4. The polyurethane foam according to claim 1 , having a density ranging from about 0.3 lb/ft 3 to about 5.0 lb/ft 3 , and exhibiting a percent modern carbon (pMC) value of ranging from about 10% to about 50% as determined by ASTM-D6866-11.
5. The polyurethane foam according to claim 1 , wherein the foam product has a bio-based content ranging from about 15% to about 30%, as determined by ASTM D6866-11.
6. The flame-retardant polyurethane foam according to claim 1 , wherein the polyurethane foam meets or exceeds the conditions of acceptance of the ICC-ES AC377 Appendix X specification.
7. A method of making a flame-retardant polyurethane foam comprising:
a. providing a first aqueous solution consisting of:
an untreated natural polyol in which substantially all of the hydroxyl groups are free,
a surfactant,
polyurethane forming catalysts,
optionally, a non-halogenated inorganic hydrate or inorganic hydroxide flame retardant,
optionally, a plasticizer,
optionally, an emulsifier,
optionally, any one of more of a halogenated or non-halogen containing blowing agent, a biocide, a bacteriostat, a polyether polyol, a filler, a colorant, an anti-scorching agent, a chain extender/cross-linker, an antioxidant, an antistatic agent, and/or a cell-opening agent,
and water,
b. combining the first aqueous solution mixture and a second solution consisting of:
a polyisocyanate,
optionally, a non-halogenated inorganic hydrate or inorganic hydroxide flame retardant, and
optionally, a plasticizer; and
c. allowing the mixture to foam;
wherein one or both of the first aqueous solution and the second solution includes the non-halogenated inorganic hydrate or inorganic hydroxide flame retardant, and one or both of the first aqueous solution and the second solution includes the plasticizer; and
wherein the first aqueous solution and the second solution are used in amounts to provide an Isocyanate Index of 20 to 50.
8. The method of claim 7 , wherein the plasticizer is added to both the first aqueous solution and the second solution.
9. The method of claim 7 , wherein the flame-retardant polyurethane foam meets or exceeds the conditions of acceptance of the ICC-ES AC377 Appendix X specification.
10. A method for preparing a water-blown, low density, polyurethane foam, the method which comprises:
contacting a first reaction mixture consisting of at least one polyisocyanate with a second reaction mixture consisting of at least one natural polyol, a blowing agent composition consisting of at least 0.1 wt % water, an effective amount of a gelling catalyst, a non-halogenated inorganic hydrate or inorganic hydroxide flame retardant, and optionally one of more of a chain extender, an emulsifier, an inorganic compound, a filler, a colorant, an anti-scorching agent, and/or glycerine,
wherein contacting occurs for a period of time sufficient to produce a polyurethane foam, the foam having a density of 0.3 lb/ft 3 to 1 lb/ft 3 ; and
wherein the first reaction mixture and the second reaction mixture are contacted in an amount sufficient to provide an Isocyanate Index of 20 to 50.
11. The method of claim 10 , wherein the halogenated or non-halogen containing blowing agent is a hydrofluorocarbon, hydrofluoro(chloro)olefin, or hydrocarbon blowing agent.
12. The method of claim 10 , wherein the at least one natural polyol is selected from the group consisting of sucrose, corn syrup, dextrose, fructose, glucose, molasses, and combinations thereof.
13. The method of claim 10 , wherein the water-blown, low density, polyurethane foam meets or exceeds the conditions of acceptance of the ICC-ES AC377 Appendix X specification.
14. A flame-retardant polyurethane foam comprising the reaction product of:
a first reaction mixture consisting of at least one polyisocyanate; and
a second reaction mixture consisting of:
a natural polyol wherein substantially all of the hydroxyl groups on the polyol are free;
a non-halogenated inorganic hydrate or inorganic hydroxide flame retardant;
a surfactant;
an aqueous blowing agent;
a polyurethane producing catalyst;
a chain extender; and
a plasticizer;
wherein the first reaction mixture and the second reaction mixture are used in amounts to provide an Isocyanate Index of 20 to 50.
15. The polyurethane foam according to claim 14 , wherein:
the natural polyol is present in the second reaction mixture at about 20-70 wt %;
the non-halogenated inorganic hydrate or inorganic hydroxide flame retardant is present in the second reaction mixture at about 5-40 wt %;
the surfactant is present in the second reaction mixture at about 1.0-5 wt %;
the aqueous blowing agent is present in the second reaction mixture at about 0.05-10 wt %;
the polyurethane producing catalyst is present in the second reaction mixture at about 0.01-10 wt %;
the chain extender is present in the second reaction mixture at about 0.5-5 wt %; and
the plasticizer is present in the second reaction mixture at about 0.01-15 wt %.