View Patent ↗A carbon-containing lithium titanium oxide containing spherical particle aggregate with a diameter of 1-80 μm, consisting of lithium titanium oxide primary particles coated with carbon. Also, a method for the production of such a carbon-containing lithium titanium oxide as well as an electrode containing such a carbon-containing lithium titanium oxide as active material as well as a lithium-ion secondary battery containing an above-described electrode.
1. A method for the production of a calcined carbon-containing lithium titanium oxide-containing spherical particle aggregates with a diameter of from 1 to 80 μm, comprising the steps of:
(a) mixing (1) a lithium salt, LiOH or Li 2 O, (2) a titanium oxide and (3) a carbon-containing compound in a solvent;
(b) drying the mixture from step a) by spray drying in a temperature gradient; and
(c) calcining the dried mixture obtained in step (b) to obtain calcined carbon-containing lithium titanium oxide-containing spherical particle aggregates with a diameter of from 1 to 80 μm.
2. The method of claim 1 , wherein the solvent is water.
3. The method of claim 2 , having an atomic ratio Li/Ti of 4:5.
4. The method of claim 2 , wherein the lithium salt is selected from the group consisting of LiNO 3 , LiHCO 3 , and LiCH 3 COO.
5. The method of claim 3 , wherein the TiO 2 in anatase form or in amorphous form is used.
6. The method of claim 5 , wherein the carbon-containing compound is selected from the group consisting of hydrocarbons, carbohydrates, and polymers.
7. The method of claim 6 , wherein the carbon-containing compound is selected from the group consisting of lactose, sucrose and saccharose.
8. The method according to claim 1 , wherein the calcined carbon-containing lithium titanium oxide containing spherical particle aggregates produced by the method have a BET surface area in the range of from 1-10 m 2 /g.
9. The method of claim 1 , wherein the spray drying is carried out in a temperature gradient falling within a range of from 90-350° C.
10. The method of claim 1 , wherein the calcining is carried out at a temperature of from 700 to 1000° C. under protective atmosphere.
11. The method according to claim 1 , wherein the calcined carbon-containing lithium titanium oxide-containing spherical particle aggregates produced by the method have a primary particle size of <1 μm.
12. The method according to claim 1 further comprising making an electrode with the calcined carbon-containing lithium titanium oxide-containing spherical particle aggregates obtained in step (c).
13. The method according to claim 12 further comprising making a lithium ion secondary battery with the electrode obtained in claim 12 .
14. The method according to claim 13 , wherein the lithium ion secondary battery obtained according to claim 13 has a charge/discharge capacity at C/10 of >165 mAh/g.