Oxidation protected separator
View Patent ↗A battery separator for a lead/acid battery is resistant to oxidation arising from the use of water or acid containing contaminants, for example chromium (Cr), manganese (Mn), titanium (Ti), copper (Cu), and the like. The separator is a microporous membrane including a rubber. The rubber is no more than about 12% by weight of the separator. The rubber may be rubber latex, tire crumb, and combinations thereof. The rubber may be impregnated into the microporous membrane. The microporous membrane may be a microporous sheet of polyolefin, polyvinyl chloride, phenol-formaldehyde resins, cross-linked rubber, or nonwoven fibers. A method for preventing the oxidation and/or extending battery life of the separator is also included.
1. A method of preventing or reducing separator oxidation in a flooded lead/acid battery arising from the use of water or acid containing contaminants comprising the steps of:
providing a dry charge lead/acid battery;
providing a microporous membrane within said dry charge lead/acid battery, said membrane impregnated with an uncross-linked or uncured rubber in the lead/acid battery, wherein said microporous membrane comprises a microporous sheet of polyolefin, polyvinyl chloride, phenol-formaldehyde resins, cross-linked rubber, or nonwoven fibers, and
adding water or acid containing contaminants, said contaminants including chromium, manganese, titanium, and combinations thereof to said dry charge battery thereby flooding the battery and subjecting the microporous membrane to said contaminants.
2. The method of claim 1 wherein said uncross-linked or uncured rubber comprising: no more than about 12% by weight of the separator.
3. The method of claim 1 wherein said uncross-linked or uncured rubber comprises about 2-4% by weight of the separator.
4. The method of claim 1 wherein said uncross-linked or uncured rubber being selected from the group consisting of rubber latex, and rubber latex and tire crumb.
5. The method of claim 1 wherein the contaminants further including copper in combination with the aforementioned contaminants.
6. The method of claim 1 , wherein said microporous membrane comprises a sheet of polyethylene.
7. The method of claim 6 , wherein said microporous membrane comprises a sheet of silica filled polyethylene.
8. A method of preventing or reducing separator oxidation in a flooded lead/acid battery arising from the use of water or acid containing contaminants including one or more of chromium, manganese, titanium, copper, and combinations thereof comprising the steps of:
providing a dry charge lead/acid battery;
providing a microporous membrane within said dry charge lead/acid battery, said membrane including an uncross-linked or uncured rubber in the lead/acid battery, wherein said microporous membrane comprises a microporous sheet of polyolefin, polyvinyl chloride, phenol-formaldehyde resins, cross-linked rubber, or nonwoven fibers, and
adding water or acid containing contaminants, said contaminants including chromium, manganese, titanium, and combinations thereof to said dry charge battery thereby flooding the battery and subjecting the microporous membrane to said contaminants.
9. The method of claim 8 wherein said uncross-linked or uncured rubber being selected from the group consisting of rubber latex, tire crumb, and combinations thereof.
10. The method of claim 8 wherein the contaminants further including copper in combination with the aforementioned contaminants.