Display for mobile device with abrasion resistant siloxane coating
View Patent ↗An abrasion resistant coating ( 206 ) is applied to a display ( 202 ) of a mobile device ( 200 ). In an embodiment, the coating ( 140 ) includes a first layer ( 106 B) including siloxane; a second layer ( 106 A) including siloxane, wherein the second layer has opposing sides and a hardness greater than the first layer; and a third layer ( 104 ) including an amorphous carbon selected from a diamond-like carbon and a diamond-like nano-composite. The first layer ( 106 B) and third layer ( 104 ) are positioned on opposing sides of the second layer ( 106 A). The third layer ( 104 ) has a hardness greater than the second layer ( 106 A).
1. A film comprising:
a substrate;
a siloxane layer comprising a siloxane-organic interpenetrating network contacting the substrate, the siloxane layer having a hardness greater than a hardness of the substrate;
another siloxane layer comprising a siloxane-organic interpenetrating network contacting the siloxane layer, the another siloxane layer having a hardness greater than the hardness of the siloxane layer, the siloxane layer and the another siloxane layer having a combined thickness of at least 20 microns; and
a diamond-like nano-composite layer comprising an amorphous carbon and a siloxane contacting the another siloxane layer, the diamond-like nano-composite layer having a hardness greater than the hardness of the another siloxane layer.
2. The film of claim 1 , wherein the substrate is a plastic.
3. The film of claim 2 , wherein the substrate is selected from the group consisting of poly(methyl methacrylate), polycarbonate, and co-extrusions of poly(methyl methacrylate) and polycarbonate.
4. The film of claim 1 , wherein the substrate is flexible.
5. The film of claim 1 , wherein the another siloxane layer has a thickness between 5 microns to 25 microns.
6. The film of claim 1 , further comprising a hydrophobic treatment layer contacting the diamond-like nano-compo site layer.
7. The film of claim 1 , wherein the combined thickness is less than 75 microns.
8. The film of claim 1 , wherein the amorphous carbon is an amorphous hydrogenated diamond-like carbon.
9. The film of claim 1 , wherein the siloxane layer or the another siloxane layer comprise an interpenetrating network of a siloxane and an acrylic.
10. The film of claim 1 , wherein the diamond-like nano-composite layer has a thickness between 3 microns and 20 microns.
11. A method of producing a film for a substrate comprising:
providing the substrate;
applying a siloxane layer comprising a siloxane-organic interpenetrating network contacting the substrate, the siloxane layer having a hardness greater than a hardness of the substrate;
applying another siloxane layer comprising a siloxane-organic interpenetrating network contacting the siloxane layer, the another siloxane layer having a hardness greater than the hardness of the siloxane layer, the siloxane layer and the another siloxane layer having a combined thickness of at least 20 microns; and
applying a diamond-like nano-composite layer comprising an amorphous carbon and a siloxane contacting the another siloxane layer, the diamond-like nano-composite layer having a hardness greater than the hardness of the another siloxane layer.
12. The method of claim 11 , wherein the substrate is a co-extrusion of poly(methyl methacrylate) and polycarbonate.
13. The method of claim 11 , wherein the substrate is a plastic lens.
14. The method of claim 11 , wherein the substrate is affixed to a plastic lens.
15. The method of claim 11 , wherein the substrate is affixed to a touch screen and display assembly.
16. The method of claim 11 , wherein the siloxane layer and the another siloxane layer have a combined thickness of less than 75 microns.
17. The method of claim 11 , wherein the diamond-like nano-composite layer is applied to the siloxane layer by a chemical vapor deposition process.
18. The method of claim 17 , wherein the chemical vapor deposition process is selected from ion beam plasma enhanced chemical vapor deposition and plasma enhanced chemical vapor deposition.
19. The method of claim 11 , wherein the siloxane layer comprises an interpenetrating network of a siloxane and an acrylic.
20. The method of claim 11 , wherein the siloxane layer comprises from 25 wt.% to 50 wt.% siloxane.