Low temperature battery with molten sodium-FSA electrolyte
View Patent ↗The present invention provides a molten sodium secondary cell. In some cases, the secondary cell includes a sodium metal negative electrode, a positive electrode compartment that includes a positive electrode disposed in a molten positive electrolyte comprising Na-FSA (sodium-bis(fluorosulonyl)amide), and a sodium ion conductive electrolyte membrane that separates the negative electrode from the positive electrolyte. One disclosed example of electrolyte membrane material includes, without limitation, a NaSICON-type membrane. Non-limiting examples of the positive electrode include Ni, Zn, Cu, or Fe. The cell is functional at an operating temperature between about 100° C. and about 150° C., and preferably between about 110° C. and about 130° C.
1. A molten sodium secondary cell, comprising:
a sodium metal negative electrode, which electrochemically oxidizes to release sodium ions during discharge and electrochemically reduces sodium ions to sodium metal during recharging;
a positive electrode compartment comprising a positive electrode disposed in a molten positive electrolyte, wherein the positive electrode comprises a metal “M”, and the metal M is selected from the group consisting of Ni, Zn, Cu, and Fe, and wherein the molten positive electrolyte consists of Na-FSA (sodium bis(fluorosulfonyl)amide) and a salt of an oxidized form of the metal M and FSA; and
a sodium ion conductive electrolyte membrane comprising a NaSICON material that separates the sodium metal negative electrode from the molten positive electrolyte,
wherein the cell has a temperature between 100° C. and 150° C. such that the sodium metal negative electrode is molten and in contact with the conductive electrolyte membrane.
2. The secondary cell of claim 1 , wherein M is Ni.
3. The secondary cell of claim 1 , wherein the NaSICON material comprises a composite membrane having a porous layer and a dense functional layer.
4. The secondary cell of claim 1 , wherein the cell has a temperature between 110° C. and 130° C.
5. The secondary cell of claim 1 , further comprising a heat management system to control the temperature of the cell.
6. A molten sodium secondary cell, comprising:
a negative electrode compartment comprising a sodium metal negative electrode, which electrochemically oxidizes to release sodium ions during discharge and electrochemically reduces sodium ions to sodium metal during recharging;
a positive electrode compartment comprising a positive electrode disposed in a molten positive electrolyte comprising Na-FSA (sodium bis(fluorosulfonyl)amide), wherein the positive electrode comprises Ni and Ni(FSA) 2 ; and
a sodium ion conductive electrolyte membrane comprising a NaSICON material that separates the sodium metal negative electrode from the molten positive electrolyte,
wherein the cell has a temperature between 110° C. and 130° C. such that the sodium metal negative electrode is molten and in contact with the conductive electrolyte membrane.
7. The secondary cell of claim 6 , wherein the NaSICON material comprises a composite membrane having a porous layer and a dense functional layer.
8. The secondary cell of claim 6 , further comprising a heat management system to control the temperature of the cell.
9. The secondary cell of claim 6 , further comprising a heat management system disposed in the negative electrode compartment to control the temperature of the negative electrode compartment.
10. The secondary cell of claim 6 , further comprising a heat management system disposed in the positive electrode compartment to control the temperature of the positive electrode compartment.
11. A molten sodium secondary cell, comprising:
a negative electrode compartment comprising a molten sodium metal negative electrode, which electrochemically oxidizes to release sodium ions during discharge and electrochemically reduces sodium ions to sodium metal during recharging;
a positive electrode compartment comprising a positive electrode comprising a metal “M”, Wherein M is selected from Ni, Zn, Cu, or Fe, disposed in a molten positive electrolyte consisting of Na-FSA (sodium bis(fluorosulfonyl)amide) and a salt of an oxidized form of the metal M and FSA, wherein the salt is selected from Ni(FSA) 2 , Zn(FSA) 2 , Cu(FSA) 2 , or Fe(FSA) 2 ; and
a sodium ion conductive electrolyte membrane comprising a NaSICON material that separates the sodium metal negative electrode from the molten positive electrolyte, wherein the cell has a temperature between 100° C. and 150° C. such that the sodium metal negative electrode is molten and in contact with the conductive electrolyte membrane.
12. The secondary cell of claim 11 , wherein M is Zn.
13. The secondary cell of claim 11 , wherein M is Cu.
14. The secondary cell of claim 11 , wherein M is Fe.
15. The secondary cell of claim 11 , wherein the NaSICON material comprises a composite membrane having a porous layer and a dense functional layer.
16. The secondary cell of claim 11 , wherein the cell functions when the temperature is between 110° C. and 130° C.
17. The secondary cell of claim 11 , further comprising a heat management system to control the temperature of the cell.
18. The secondary cell of claim 11 , wherein M is Ni and the salt is Ni(FSA) 2 .
19. The secondary cell of claim 11 , wherein M is Zn and the salt is Zn(FSA) 2 .
20. The secondary cell of claim 11 , wherein M is Cu and the salt is Cu(FSA) 2 .
21. The secondary cell of claim 11 , wherein M is Fe and the salt is Fe(FSA) 2 .