Thin-walled implant structures and related methods
View Patent ↗Ceramic implants, such as spinal implants, may comprise a dense shell and a porous core. In some implementations, methods for manufacturing the implants may comprise one or more stages at which the core material abuts the shell so as to form a mechanical attachment therewith while both the core and the shell are in a green state. The core and the shell may be fired together, and the resultant implant may, in some embodiments, comprise a unitary piece of ceramic material. Some embodiments may comprise silicon nitride ceramic materials.
1. A method for manufacturing a ceramic intervertebral spacer, the method comprising the steps of:
providing a ceramic tape in a green state;
forming a shell at least partially defining a cavity using the ceramic tape;
preparing a slurry comprising a ceramic powder;
decreasing a density of the slurry;
introducing the slurry into the cavity;
gelating the slurry to form a gelled slurry;
drying the gelled slurry within the cavity; and
firing the shell in a green state and the dried slurry together such that the combined shell and dried slurry comprise a fired unitary ceramic intervertebral spacer.
2. The method of claim 1 , wherein the step of gelating the slurry to form a gelled slurry comprises activating a gelation agent in the slurry.
3. The method of claim 1 , wherein the shell defines a closed loop.
4. The method of claim 1 , wherein the slurry comprises a foaming agent, and wherein the step of decreasing the density of the slurry comprises activating the foaming agent.
5. The method of claim 1 , wherein the shell of the ceramic intervertebral spacer comprises a first density, wherein the dried slurry comprises a second density, and wherein the first density is greater than the second density.
6. The method of claim 1 , wherein the step of gelating the slurry to form a gelled slurry is performed after the step of introducing the slurry into the cavity.
7. The method of claim 1 , wherein an average thickness of the shell after firing is between about 50 microns and about 150 microns.
8. The method of claim 1 , wherein the ceramic powder comprises a silicon nitride ceramic powder, and wherein the ceramic tape comprises a silicon nitride ceramic tape.
9. A method for manufacturing a ceramic intervertebral spacer, the method comprising the steps of:
positioning a rod member within a first cavity to define an at least substantially annular cavity within a mold;
performing a first gelcasting process to create a shell for a ceramic intervertebral spacer within the at least substantially annular cavity;
removing the rod member such that the shell defines a second cavity;
performing a second gelcasting process to create an inner layer within the second cavity;
drying the shell and the inner layer together; and
firing the shell and the inner layer together to form a unitary ceramic intervertebral spacer.
10. The method of claim 9 , wherein the rod member comprises a mandrel.
11. The method of claim 9 , wherein the inner layer comprises a density less than a density of the shell.
12. The method of claim 9 , wherein the inner layer comprises a core of the ceramic intervertebral spacer.
13. The method of claim 12 , wherein the core comprises a porosity that at least substantially mimics that of natural cancellous bone to facilitate bone ingrowth with the core.
14. The method of claim 13 , wherein the shell comprises a porosity that at least substantially mimics that of natural cortical bone.
15. The method of claim 9 , further comprising:
performing a third gelcasting process to create a second inner layer positioned within the inner layer;
drying the shell, the inner layer, and the second inner layer together;
and
firing the shell, the inner layer, and the second inner layer together to form a unitary ceramic intervertebral spacer.
16. The method of claim 15 , wherein the second inner layer comprises a core of the ceramic intervertebral spacer, and wherein the inner layer comprises a density in between a density of the shell and the core.
17. The method of claim 9 , wherein the step of performing a first gelcasting process comprises:
preparing a slurry comprising a ceramic powder and a gelation agent;
introducing the slurry into the at least substantially annular cavity of the mold; and
activating the gelation agent to form a gelled slurry.
18. The method of claim 9 , wherein the shell comprises a silicon nitride ceramic material, and wherein the inner layer comprises a silicon nitride ceramic material.
19. The method of claim 9 , wherein the shell comprises an average thickness after firing of between about 0.25 mm and about 2 mm.
20. A method for manufacturing a silicon nitride ceramic intervertebral spacer, the method comprising the steps of:
preparing a first slurry comprising a silicon nitride ceramic powder and a gelation agent;
preparing a second slurry comprising a silicon nitride ceramic powder, a gelation agent, and a foaming agent,
introducing the first slurry into a first mold;
introducing the second slurry into a second mold defined by the first slurry such that the first and second slurries are in contact;
gelating the first slurry to form a first gelled slurry;
activating the foaming agent in the second slurry such that a porosity of the second slurry is higher than a porosity of the first slurry;
gelating the second slurry to form a second gelled slurry;
drying the first gelled slurry and the second gelled slurry together while the first gelled slurry is in contact with the second gelled slurry such that the first gelled slurry forms a compact comprising a shell and the second gelled slurry forms a compact comprising a core positioned within the shell; and
firing the shell and the core together to form a unitary, silicon nitride ceramic intervertebral spacer.
21. The method of claim 20 , wherein the step of gelating the second slurry is performed after the step of gelating the first slurry.